BJB Polyurethane TC-8764 A/B
| Category: | TSU , Polyurethane Thermoset Elastomer |
| Manufacturer: | BJB Enterprises, Inc. |
| Trademark: | BJB Polyurethane |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bod8zG_BJB-Polyurethane-TC-8764-A-B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TC-8764 A/B is a two-component urethane casting compound that is specifically formulated for high abrasion and impact resistance. It is recommended for use for the production casting of highly wear-resistant parts and linings. This product is a safe, easy-to-handle, room temperature mixing and curing system that does not contain TDI, MDI, MDA or MOCA. TC-8764 A/B is relatively insensitive to typical environmental moisture and will make good void-free parts without the problems that some conventional urethane systems exhibit. Because of this products exceptional toughness and abrasion resistance, castings made with TC-8764 A/B are particularly suitable for mining and mineral process industries. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- 1 | 1.09 | g/cm³ | |
| -- | 1.13 | g/cm³ | ASTM D792 |
| -- 2 | 1.14 | g/cm³ | |
| Specific Volume | 0.903 | cm³/g | |
| Color | |||
| Part A | Pale Yellow | ||
| Part B | Amber |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gel Time | 15.0 to 20.0 | min | |
| Work Time (25°C) 3 | 10.0 to 15.0 | min |
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage - Flow | 0.90 | % | ASTM D2566 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 58 to 62 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 283 | MPa | ASTM D638 |
| Tensile Strength | 30.3 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 310 | % | ASTM D638 |
| Flexural Modulus | 267 | MPa | ASTM D790A |
| Flexural Strength | 9.86 | MPa | ASTM D790A |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength | 89.3 | kN/m | ASTM D624 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | > 530 | J/m | ASTM D256 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 100, Mix Ratio by Volume: 100 | ||
| Part B | Mix Ratio by Weight: 50, Mix Ratio by Volume: 48 | ||
| Shelf Life (24°C) | 26 | wk | |
| Thermoset Mix Viscosity | ASTM D2393 | ||
| 25°C 4 | 250 | cP | |
| 25°C 5 | 2750 | cP | |
| 25°C 6 | 1550 | cP | |
| Demold Time (25°C) | 120 to 180 | min | |
| Post Cure Time (25°C) | 120 to 170 | hr |
| Note Message | |
|---|---|
| 1 . | Part A |
| 2 . | Part B |
| 3 . | 100g mass |
| 4 . | Part B, Brooksfield |
| 5 . | Part A, Brooksfield |
| 6 . | Mixed, Brooksfield |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Therma-Tech™ TT9200-8705 EI Black | PolyOne Corporation | PPS | Therma-Tech™ |
| 陶氏低密度聚乙烯 615C | The Dow Chemical Company | LDPE | DOW™ LDPE |
| Next Nylon 6 Prime Series NGBMS1 35-01BK | Next Polymers Ltd. | Nylon 6 | Next Nylon 6 Prime Series |
| Chemlon® 204-13 GVNH BK083 | Teknor Apex Company (Chem Polymer) | Nylon 6 | Chemlon® |
| Durez® 23570 (Compression) | Sumitomo Bakelite North America, Inc. | Phenolic | Durez® |