Kingfa JH960 HT10
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Kingfa |
| Trademark: | Kingfa |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bnZw8D_Kingfa-JH960-HT10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Kingfa JH960 HT10 is a polycarbonate acrylonitrile butadiene styrene (PC ABS) material,. This product is available in North America or Asia Pacific region. The processing method is injection molding. The main features of Kingfa JH960 HT10 are:
Typical application areas include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 21 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (23°C) | 0.50 - 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 58.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 60 | % | ASTM D638 |
| Flexural Modulus 3 | 2500 | MPa | ASTM D790 |
| Flexural Strength 4 | 90.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -10°C, 3.20 mm | 320 | J/m | ASTM D256 |
| 23°C, 3.20 mm | 510 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.40mm | 121 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 105 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | ASTM D257 |
| Dielectric Strength (1.60 mm) | 19 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-0 | UL 94 | |
| 3.00 mm | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 90.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 230 - 255 | °C | |
| Middle Temperature | 230 - 260 | °C | |
| Front Temperature | 235 - 270 | °C | |
| Processing (Melt) Temp | 230 - 260 | °C | |
| Mold Temperature | 40.0 - 80.0 | °C | |
| Back Pressure | 0.300 - 0.700 | MPa |
| Injection instructions |
|---|
| Processing Temperature Limit: 275°CInjection Speed: 30 to 80% |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VAMPORAN 0024 V0 13 | Vamp Tech | PPE+PS | VAMPORAN |
| Celanex® 2402 MT | Celanese Corporation | PBT | Celanex® |
| Formolon® 676 | Formosa Plastics Corporation, U.S.A. | PVC, Flexible | Formolon® |
| EnCom GF30 PC | EnCom, Inc. | PC | EnCom |
| Vipel® F774-PTW-30 | AOC, L.L.C. | Polyester Alloy | Vipel® |