TRIBOCOMP® POM TS14
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | EPIC Polymers |
| Trademark: | TRIBOCOMP® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bnVCEV_TRIBOCOMP-POM-TS14.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TRIBOCOMP® POM TS14 is an Acetal (POM) Copolymer product. It is available in Europe. Primary characteristic: lubricated. |
| General Information | |
|---|---|
| Additive |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.37 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 2.2 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.20 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2600 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 45.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | > 10 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 2300 | MPa | ISO 178 |
| Flexural Stress (23°C) | 65.0 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 | ||
| Dynamic | 0.11 | ||
| Static | 0.10 | ||
| Wear Factor | 10.0 | ASTM D3702 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 55 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 150 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 105 | °C | ISO 75-2/A |
| CLTE - Flow (23°C) | 1.0E-4 | cm/cm/°C | ISO 7991 |
| Thermal Conductivity | 0.23 | W/m/K | ISO 22007 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | ASTM D257 |
| Electric Strength | 35 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 160 to 210 | °C | |
| Middle Temperature | 170 to 220 | °C | |
| Front Temperature | 180 to 220 | °C | |
| Nozzle Temperature | 200 to 225 | °C | |
| Processing (Melt) Temp | < 220 | °C | |
| Mold Temperature | 80.0 to 120 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RapidVac™ VA-1515 | Innovative Polymers, Inc. | TSU | RapidVac™ |
| AKROMID® B3 GF 15 1 L natural (4690) | AKRO-PLASTIC GmbH | Nylon 6+PP | AKROMID® |
| ASTALOY™ PC/ABS EHA | Marplex Australia Pty. Ltd. | PC+ABS | ASTALOY™ |
| Kepamid® 1300CRK | Korea Engineering Plastics Co., Ltd | Nylon 6 | Kepamid® |
| LNP™ STAT-KON™ DE0049P compound | SABIC Innovative Plastics | PC | LNP™ STAT-KON™ |