LNP™ FARADEX™ WX94736 compound
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ FARADEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bnCz7C_LNP-FARADEX-WX94736-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* FARADEX* WX94736 is a compound based on PBT resin containing Stainless Steel. Added features of this material include: EMI/RFI Shielding, Electrically Conductive. Also known as: LNP* FARADEX* Compound PDX-W-94736 Product reorder name: WX94736 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.51 | g/cm³ | ASTM D792 |
| -- | 1.50 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.80 to 1.0 | % | ASTM D955 |
| Across Flow : 24 hr | 1.0 to 1.2 | % | ASTM D955 |
| Across Flow : 24 hr | 1.1 | % | ISO 294-4 |
| Flow : 24 hr | 0.89 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.10 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 3450 | MPa | ASTM D638 |
| -- | 3110 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 53.8 | MPa | ASTM D638 |
| Yield | 53.0 | MPa | ISO 527-2 |
| Break | 53.8 | MPa | ASTM D638 |
| Break | 53.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 2.7 | % | ASTM D638 |
| Yield | 2.8 | % | ISO 527-2 |
| Break | 2.8 | % | ASTM D638 |
| Break | 2.9 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2760 | MPa | ASTM D790 |
| -- | 3100 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 55.2 | MPa | ASTM D790 |
| -- | 83.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 59 | J/m | ASTM D256 |
| 23°C 2 | 6.1 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 610 | J/m | ASTM D4812 |
| 23°C 3 | 23 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 6.20 | J | ASTM D3763 |
| -- | 1.90 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 144 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 4 | 147 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 99.4 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 5 | 123 | °C | ISO 75-2/Af |
| CLTE | |||
| Flow : -40 to 40°C | 8.3E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Transverse : -40 to 40°C | 6.8E-5 | cm/cm/°C | ASTM E831 |
| Transverse : -40 to 40°C | 6.9E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 2.0 to 6.0 | ohms | ASTM D257 |
| Volume Resistivity | 3.0 to 7.0 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 221 to 232 | °C | |
| Middle Temperature | 243 to 254 | °C | |
| Front Temperature | 260 to 271 | °C | |
| Processing (Melt) Temp | 238 to 266 | °C | |
| Mold Temperature | 82.2 to 98.9 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Marlex® EHM 6004 | Chevron Phillips Chemical Company LLC | HDPE | Marlex® |
| UBESTA XPA 9044 X2 | UBE Engineering Plastics, S.A. | Nylon 12 Elast | UBESTA |
| Hanwha Total PP BJ600 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP Impact Copolymer | Hanwha Total PP |
| Hanwha Total PP RP100E140 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, Unspecified | Hanwha Total PP |
| Stanyl® WTP81 | DSM Engineering Plastics | Nylon 46 | Stanyl® |