Lupolen 4261 AG UV
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Lupolen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bmCGrF_Lupolen-4261-AG-UV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Lupolen 4261 AG UV is a high density polyethylene with outstanding ESCR, high impact resistance and good chemical resistance, delivered in pellet form. Main applications* are jerry cans, heating oil tanks and IBC. *Appropriateness of resin for use in specific applications, under outdoor or indoor storage conditions or for specific container contents should be carried out by the appropriate parties (converter, end user) on the molded item with reference to appropriate local, national and international guidelines. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.945 | g/cm³ | ISO 1183 |
| Apparent Density | > 0.50 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/21.6 kg | 6.0 | g/10 min | |
| 190°C/5.0 kg | 0.35 | g/10 min | |
| Basell Bottle Test | 5.5 | month |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Staudinger Index - Jg | 370 | cm³/g | ISO 1628 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 132/30) | 40.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 850 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 24.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 10 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Impact Strength (-30°C) | 170 | kJ/m² | ISO 8256/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 70.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 42.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 125 | °C | ISO 306/A50 |
| -- | 75.0 | °C | ISO 306/B50 |
| Melting Temperature (DSC) | 130 | °C | ISO 3146 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Electric Strength 1 | > 150 | kV/mm | IEC 60243-1 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 180 to 220 | °C |
| Note Message | |
|---|---|
| 1 . | K20/P50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTV-2 GI-1100 | Silicones, Inc. | Silicone Rubber, RTV-2 | RTV-2 |
| ETILINAS LL0220SA | POLYETHYLENE MALAYSIA SDN BHD | LLDPE | ETILINAS |
| Karina BEIGE COLOR CONCENTRATE -E 08/26-FC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| SABIC® LDPE PCG06 | Saudi Basic Industries Corporation (SABIC) | LDPE | SABIC® LDPE |
| Sumiliteresin® PR-103 I | SBHPP | Phenolic | Sumiliteresin® |