POLYNIL® C50L
| Category: | Nylon 66/6 , Polyamide 66/6 Copolymer |
| Manufacturer: | Nilit Plastics |
| Trademark: | POLYNIL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | blzLBU_POLYNIL-C50L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
POLYNIL® C50L is an unreiforced Polyamide 66/6 (Nylon 66/6) copolymer for injection molding. This general pourpose 2.7 viscosity Polyamide 66/6 resin is FDA compliant. |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.13 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow : 23°C | 1.7 | % | |
| Flow : 23°C | 1.5 | % | |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 1.5 | % | |
| Saturation, 23°C | 8.5 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2900 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 80.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield, 23°C | 8.0 | % | |
| Break, 23°C | 80 | % | |
| Flexural Modulus (23°C) | 2500 | MPa | ISO 178 |
| Flexural Stress (23°C) | 110 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 5.5 | kJ/m² | |
| 23°C | 6.5 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| 23°C | No Break | ||
| 30°C | No Break | ||
| Notched Izod Impact Strength (23°C) | 6.0 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 210 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 65.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 220 | °C | ISO 306/B |
| Ball Pressure Test | IEC 60695-10-2 | ||
| 125°C | Pass | ||
| 165°C | Pass | ||
| Melting Temperature | 249 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity 1 | 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength (2.00 mm) | 18 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index (3.20 mm, Solution A) | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 28 | % | ISO 4589-2 |
| Flammability 2 | SE | FMVSS 302 |
| Note Message | |
|---|---|
| 1 . | 23°C |
| 2 . | 355x100x1mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nycal™ 2155R14T1 | Technical Polymers, LLC | Nylon 66 | Nycal™ |
| EPLAMID 66 GFS 15 HS NC | EPSAN Plastik SAN. ve TiC. A.S. | Nylon 66 | EPLAMID 66 |
| LNP™ VERTON™ EV008 compound | SABIC Innovative Plastics | PEI | LNP™ VERTON™ |
| OpteSTAT™ PA6,6 DP502 | Ovation Polymers Inc. | Nylon 66 | OpteSTAT™ |
| POLYelast TPE EC90 D50 P05B | Polykemi AB | PP+EPDM | POLYelast |