Epocast 1629 A/B
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Huntsman Advanced Materials |
| Trademark: | Epocast |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bl8rtA_Epocast-1629-A-B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| DESCRIPTION: Epocast® 1629-A/B epoxy syntactic is a beige-tan, self-extinguishing, ultra-low density system for edge reinforcing of honeycomb structures. It can be extruded or spread with a putty knife and resists slumping on vertical surfaces. Epocast® 1629-A/B epoxy syntactic sands and machines easily when cured. It is a non-PBDE containing material and can be used as a replacement for Epocast® 87005 A/B-80 epoxy syntactic, Epocast® 87005 A/B-60 epoxy syntactic, Epocast® 87269 A/B epoxy syntactic, Epocast® 87005 A/B-61 epoxy syntactic, and Epocast® 87005 A/BE- 60 epoxy syntactic. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D1622 | ||
| -- 1 | 0.420 | g/cm³ | ASTM D1622 |
| -- 2 | 0.480 | g/cm³ | ASTM D1622 |
| -- 3 | 0.520 | g/cm³ | ASTM D1622 |
| Viscosity | ASTM D2196 | ||
| -- 4 | Paste | ASTM D2196 | |
| -- 5 | Paste | ASTM D2196 | |
| -- 6 | Paste | ASTM D2196 |
| Flammability | Nominal Value | Unit | |
|---|---|---|---|
| Flammability 7 | |||
| Burn Length | 2.54 | cm | |
| self-extenguishing | 2.0 | sec |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gel Time - 75 gms (25°C) | 1.2 | hr | ASTM D2471 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Cure Time (25°C) | 2.0 | day | |
| Tensile Lap Shear - etched al/al (25°C) | 7.58 | MPa | ASTM D1002 |
| Weight Gain 8 | ASTM D543 | ||
| Distilled water : 25°C | 2.3 | % | ASTM D543 |
| Mil-M-5606, hydraulic fluid : 25°C | 1.5 | % | ASTM D543 |
| Mil-S-3136, Type III test fluid : 25°C | 0.60 | % | ASTM D543 |
| Skydrol 500-A : 25°C | 3.0 | % | ASTM D543 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Compressive Modulus | 1380 | MPa | ASTM D695 |
| Compressive Strength (25°C) | 20.7 | MPa | ASTM D695 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Resin | Mixing ratio by weight: 100 | ||
| Hardening method | Mixing ratio by weight: 50 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| CURE SCHEDULE: 48 hours at 77°F (25°C), or gel at room temperature plus 5 hours at 125°F (52°C). |
| Note Message | |
|---|---|
| 1 . | Hardener |
| 2 . | System |
| 3 . | Resin |
| 4 . | Resin |
| 5 . | Hardener |
| 6 . | System |
| 7 . | 12-second vertical |
| 8 . | on immersion - 24 hrs |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NANCAR® 1072 | Nantex Industry Co., Ltd. | NBR | NANCAR® |
| Akulon® K224-G4U | DSM Engineering Plastics | Nylon 6 | Akulon® |
| Desmopan® DP 6080A | Covestro - PUR | TPU, Unspecified | Desmopan® |
| Di-Pak™ E-4595 | Hapco Inc. | TP, Unspecified | Di-Pak™ |
| Elvax® 550A | DuPont Packaging & Industrial Polymers | EVA | Elvax® |