Ultramid® T KR 4355 G5
| Category: | Nylon 6/6T , Polyamide 6/6T Copolymer |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bistD4_Ultramid-T-KR-4355-G5.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Ultramid T KR 4355 G5 is a 25% glass fiber reinforced injection molding PA6/6T grade featuring high toughness, stiffness, and strength, low water absorption, and high melting point (295 C). After the material has been conditioned, its mechanical properties remain stable up to 65 C. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.35 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 5.5 | -- | % | |
| Equilibrium, 23°C, 50% RH | 1.3 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 9000 | 9000 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | |||
| Break, -40°C | 214 | 203 | MPa | |
| Break, 23°C | 185 | 170 | MPa | |
| Break, 80°C | 111 | -- | MPa | |
| Tensile Strain (Break, 23°C) | 3.0 | 3.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 7300 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | |||
| -30°C | 8.5 | -- | kJ/m² | |
| 23°C | 11 | -- | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | |||
| -30°C | 60 | -- | kJ/m² | |
| 23°C | 80 | -- | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 270 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 295 | -- | °C | ISO 3146 |
| CLTE | ||||
| Flow | 2.5E-5 | -- | cm/cm/°C | |
| Transverse | 5.5E-5 | -- | cm/cm/°C | |
| RTI Elec | UL 746 | |||
| 0.750 mm | 140 | -- | °C | |
| 1.50 mm | 140 | -- | °C | |
| 3.00 mm | 140 | -- | °C | |
| RTI Imp | UL 746 | |||
| 0.750 mm | 100 | -- | °C | |
| 1.50 mm | 115 | -- | °C | |
| 3.00 mm | 115 | -- | °C | |
| RTI Str | UL 746 | |||
| 0.750 mm | 120 | -- | °C | |
| 1.50 mm | 140 | -- | °C | |
| 3.00 mm | 140 | -- | °C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+15 | 1.0E+14 | ohms·cm | IEC 60093 |
| Dielectric Constant (1 MHz) | 4.30 | 4.50 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.030 | 0.040 | IEC 60250 | |
| Comparative Tracking Index | 600 | 600 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.440 mm | HB | -- | ||
| 0.750 mm | HB | -- | ||
| 1.50 mm | HB | -- | ||
| 3.00 mm | HB | -- |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultramid® 66 H2 G/25-V0KB1 NAT0046 | BASF Corporation | Nylon 66 | Ultramid® |
| VAMPCARB 0024 V2 | Vamp Tech | PC | VAMPCARB |
| NANTEX® 630E | Nantex Industry Co., Ltd. | NBR | NANTEX® |
| Dryflex® A1 600801 | ELASTO | SEBS | Dryflex® |
| Starflam PA12 Z31E (EXP) | Eurostar Engineering Plastics | Nylon 12 | Starflam |