Plenco 02308 (Transfer)
| Category: | Phenolic , Phenolic |
| Manufacturer: | Plastics Engineering Co. |
| Trademark: | Plenco |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bik6YM_Plenco-02308-Transfer-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PLENCO 02308 is a general purpose organic filled phenolic molding compound, offering improved heat resistance and optimized cure properties. UL recognized under component file E40654. 02308 is available in black or brown color. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.43 | g/cm³ | ASTM D792 |
| Apparent Density | 0.64 | g/cm³ | ASTM D1895 |
| Molding Shrinkage - Flow | 0.61 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.31 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (E-Scale) | 86 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8000 | MPa | ASTM D638 |
| Tensile Strength | 53.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 0.80 | % | ASTM D638 |
| Flexural Modulus | 8160 | MPa | ASTM D790 |
| Flexural Strength | 87.6 | MPa | ASTM D790 |
| Compressive Strength | 207 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 19.9 | J/m | ASTM D256 |
| Notched Izod Impact | 19 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 172 | °C | ASTM D648 |
| Continuous Use Temperature | 204 | °C | ASTM D794 |
| CLTE - Flow | 6.9E-5 | cm/cm/°C | ASTM E831 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 3.7E+11 | ohms·cm | ASTM D257 |
| Dielectric Strength 1 | 12 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 5.40 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 0.055 | ASTM D150 | |
| Arc Resistance | 143 | sec | ASTM D495 |
| Comparative Tracking Index (CTI) | 175 | V | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 | |
| Oxygen Index | 26 | % | ASTM D2863 |
| Additional Information |
|---|
| The value listed as Mold Shrink, Linear-Flow, ASTM D955 was tested according to the ASTM D6289 standard.The value listed as Comparative Tracking Index, UL 746 was tested according to ASTM D3638.Post Shrinkage, ASTM D6289, 72hr, 120°C: 0.29%Heat Resistance, ASTM D794: 204°CDrop Ball Impact, PLENCO Method: 98 J/m |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 165 - 182 | °C | |
| Back Pressure | 0.300 | MPa | |
| Screw Speed | < 60 | rpm |
| Injection instructions |
|---|
| Transfer Time: 3-8 secTransfer Pressure: 5.5-6.9 MPaPreheating Temperature: 104-115°C |
| Note Message | |
|---|---|
| 1 . | Method A (short time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sunny® PBT EB130 | Guangdong Shunde Shunyan New Material Co., Ltd. | PBT | Sunny® |
| TEREZ PC 1008 schwarz | TER HELL PLASTIC GMBH | PC | TEREZ PC |
| Alpha PVC GW 2038-A-VW1 NAT LCF | AlphaGary | PVC, Unspecified | Alpha PVC |
| Celcon® LU02 | Celanese Corporation | Acetal (POM) Copolymer | Celcon® |
| FILLMA 5002G30 | POLYROCKS CHEMICAL CO., LTD | PP, Unspecified | FILLMA |