Adsyl 7423 XCP
| Category: | Polyolefin, Unspecified , Polyolefin |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Adsyl |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | biaoqy_Adsyl-7423-XCP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Adsyl 7423 XCP is an advanced polyolefin, specially designed for use as a sealing layer in co-extruded film applications. This grade features a low seal initiation temperature. It contains anti-blocking additives. For regulatory information please refer to Adsyl 7423 XCP Product Stewardship Bulletin (PSB). |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.900 | g/cm³ | ASTM D792, ISO 1183/A |
| Melt Mass-Flow Rate (MFR) | |||
| -- | 5.5 | g/10 min | ASTM D1238 |
| 230°C/2.16 kg | 5.5 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 24.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strain (Break) | 500 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 750 | MPa | ASTM D790 |
| -- | 700 | MPa | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Tensile Modulus | ISO 527-3/25 | ||
| MD : 50 µm, Cast Film | 340 | MPa | |
| TD : 50 µm, Cast Film | 340 | MPa | |
| Tensile Stress | ISO 527-3/500 | ||
| MD : Yield, 50 µm, Cast Film | 17.0 | MPa | |
| TD : Yield, 50 µm, Cast Film | 16.0 | MPa | |
| MD : Break, 50 µm, Cast Film | 25.0 | MPa | |
| TD : Break, 50 µm, Cast Film | 35.0 | MPa | |
| Tensile Elongation | ISO 527-3/500 | ||
| MD : Yield, 50 µm, Cast Film | 15 | % | |
| TD : Yield, 50 µm, Cast Film | 14 | % | |
| MD : Break, 50 µm, Cast Film | 650 | % | |
| TD : Break, 50 µm, Cast Film | 850 | % | |
| Seal Initiation Temperature | 110 to 115 | °C |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 67.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 74.0 | °C | ASTM D648, ISO 75-2/A |
| Melting Temperature | 130 | °C | ISO 11357-3 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 50.0 µm, Cast Film) | 91 | ASTM D2457 | |
| Haze (50.0 µm, Cast Film) | 0.90 | % | ASTM D1003 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Fainplast PVC PH 58/AL | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| Kepamid® 2313GFS | Korea Engineering Plastics Co., Ltd | Nylon 66 | Kepamid® |
| Hostacom PC072-3 natural | LyondellBasell Industries | PP Homopolymer | Hostacom |
| LTP PC7100 | Chengdu Letian Plastics Co., Ltd | TP, Unspecified | LTP |
| ALCOM® MED PS 2030 07001 | ALBIS PLASTIC GmbH | PS (GPPS) | ALCOM® MED PS |