Order Products : sales@su-jiao.com
Starex LX-0981M
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | LOTTE ADVANCED MATERIALS CO., LTD. |
| Trademark: | Starex |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | biTl3l_StarexLX0981M.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Starex LX-0981M is an acrylonitrile butadiene styrene (ABS) product,. It is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Typical application areas are: electrical appliances. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity (Natural) | 1.06 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238, ISO 1133 | ||
| 200°C/5.0 kg | 5.0 | g/10 min | ASTM D1238, ISO 1133 |
| 220°C/10.0 kg | 56 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow : 3.20mm | 0.20 - 0.30 | % | ASTM D955 |
| Transverse flow : 3.20mm | 0.20 - 0.30 | % | ASTM D955 |
| Lateral flow : 3.20mm | 0.20 - 0.30 | % | ISO 2577 |
| Traffic : 3.20mm | 0.20 - 0.30 | % | ISO 2577 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| Class r | 109 | ASTM D785 | |
| R scale | 111 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2200 | MPa | ASTM D638 |
| -- | 2300 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 2 | 48.0 | MPa | ASTM D638 |
| Yield | 490 | MPa | ISO 527-2/50 |
| Fracture 3 | 36.0 | MPa | ASTM D638 |
| Fracture | 37.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Fracture 4 | 10 | % | ASTM D638 |
| Fracture | 16 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 5 | 2100 | MPa | ASTM D790 |
| -- 6 | 21700 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 64.0 | MPa | ASTM D790 |
| -- 8 | 650 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 16 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 180 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 180 | J/m | ASTM D256 |
| 23°C 10 | 17 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 6.40mm | 89.0 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 4.00mm | 79.0 | °C | ISO 75-2/B |
| 1.8 MPa, unannealed, 6.40mm | 82.0 | °C | ASTM D648 |
| 1.8 MPa, not annealed, 4.00mm | 73.0 | °C | ISO 75-2/A |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 50 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.8 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | Thickness: 4mm |
| 10 . | Thickness: 4mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| THERMOLAST® K TC8CSZ (Series: CS) | KRAIBURG TPE | TPE | THERMOLAST® K |
| WELLAMID Nylon 6600 MRGV 25/15 HWCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 66 | WELLAMID Nylon |
| NEFTEKHIM PE 2260M (601F7) | Nizhnekamskneftekhim Inc. | HDPE | NEFTEKHIM PE |
| Hostaform® LX90GC15 | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |
| Plenco 02300 (Transfer) | Plastics Engineering Co. | Phenolic | Plenco |