Clariant PC PC-1100H30
| Category: | PC , Polycarbonate |
| Manufacturer: | Clariant Corporation |
| Trademark: | Clariant PC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bhcCe3_Clariant-PC-PC-1100H30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Clariant PC PC-1100H30 is a polycarbonate (PC) material, which contains a 30% carbon fiber reinforced material. This product is available in North America and is processed by injection molding. The main features of Clariant PC PC-1100H30 are:
Typical application areas include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.33 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.15 | % | ASTM D955 |
| Water Absorption | ASTM D570 | ||
| 24 hr | 0.080 | % | ASTM D570 |
| Saturation | 0.18 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| Class m | 92 | ASTM D785 | |
| Class r | 110 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 169 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.0 | % | ASTM D638 |
| Flexural Modulus | 13800 | MPa | ASTM D790 |
| Flexural Strength | 248 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 152 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 149 | °C | ASTM D648 |
| CLTE - Flow | 1.8E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+3 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-1 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 304 - 343 | °C | |
| Middle Temperature | 304 - 343 | °C | |
| Front Temperature | 304 - 343 | °C | |
| Processing (Melt) Temp | 304 - 327 | °C | |
| Melt Temperature (Aim) | 316 | °C | |
| Mold Temperature | 82.2 - 121 | °C | |
| Injection Rate | Fast | ||
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 45 - 75 | rpm | |
| Cushion | 3.18 - 6.35 | mm |
| Injection instructions |
|---|
| The minimum injection pressure required to fill the part should be used for the first stage. The hold pressure should be set between 50% and 75% of the injection pressure. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1307 C EF L | RTP Company | PPS | RTP |
| Sinpolene MBW1331 | Teknor Apex Asia Pacific PTE. LTD. | LLDPE | Sinpolene |
| UNIVAL™ DMDC-6143 NT 7 | The Dow Chemical Company | HDPE | UNIVAL™ |
| Elvax庐 3135SB | DuPont Packaging & Industrial Polymers | EVA | Elvax® |
| LNP™ LUBRICOMP™ RX94033 compound | SABIC Innovative Plastics Europe | Nylon 66 | LNP™ LUBRICOMP™ |