NIMA HL 18400
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Ovation Polymers Inc. |
| Trademark: | NIMA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bh7tu7_NIMA-HL-18400.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High Density Polyethylene - Halogenated FR compound with good impact resistance. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 400 | MPa | ASTM D638 |
| Tensile Strength 2 | ASTM D638 | ||
| Yield | 18.0 | MPa | ASTM D638 |
| Fracture | 15.0 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 50 | % | ASTM D638 |
| Flexural Modulus 4(50.0 mm Span) | 320 | MPa | ASTM D790 |
| Flexural Strength 5(Break, 50.0 mm Span) | 16.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 190 | J/m | ASTM D256 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Additional Information |
|---|
| Tensile Elongation at Break, ASTM D638: >50% |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRE-ELEC® PE 1291 | Premix Oy | HDPE | PRE-ELEC® |
| Microthene® F FA70000 | LyondellBasell Industries | HDPE | Microthene® F |
| Starflam RX06082 | Eurostar Engineering Plastics | Nylon 66/6 | Starflam |
| Kumho EP AES HW 600G | Korea Kumho Petrochemical Co., Ltd. | AES | Kumho EP |
| Karina DARK BEIGE MBU -E 08/499-IE | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |