RTP 1106 HS
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bh2IK5_RTP-1106-HS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. -Preliminary Product Data per RTP Co.- RTP 1106 HS offers an optimum balance of strength, stiffness, toughness, heat resistance and excellent electricals. It offers good surface appearance at a very competitive cost. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.62 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.15 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.35 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 179 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.0 | % | ASTM D638 |
| Flexural Modulus | 11700 | MPa | ASTM D790 |
| Flexural Strength | 269 | MPa | ASTM D790 |
| Compressive Strength | 172 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (6.35 mm) | 91 | J/m | ASTM D256 |
| Unnotched Izod Impact (6.35 mm) | 850 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 229 | °C | ASTM D648 |
| CLTE - Flow | 2.5E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 0.30 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 22 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.70 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 0.013 | ASTM D150 | |
| Arc Resistance | 126 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.59 mm, Values per RTP Company testing.) | V-0 | UL 94 |
| Additional Information |
|---|
| Mold Shrinkage, Linear-Flow, ASTM D-955, 0.25in.: 2.5mil/in. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 135 | °C | |
| Drying Time | 3.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 260 - 299 | °C | |
| Middle Temperature | 260 - 299 | °C | |
| Front Temperature | 260 - 299 | °C | |
| Mold Temperature | 82.0 - 121 | °C | |
| Injection Pressure | 68.9 - 103 | MPa | |
| Back Pressure | 0.172 - 0.517 | MPa | |
| Clamp Tonnage | 6.9 - 11 | kN/cm² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTV-2 GI-1210 | Silicones, Inc. | Silicone Rubber, RTV-2 | RTV-2 |
| CGPC PVC SO-30X (105 phr Plasticizer E) | China General Plastics Corporation | PVC, Flexible | CGPC PVC |
| HI-ZEX™ 537B | Prime Polymer Co., Ltd. | HDPE | HI-ZEX™ |
| INEOS HDPE T60-500-119 | INEOS Olefins & Polymers USA | HDPE | INEOS HDPE |
| Pinnacle PP 2135H | Pinnacle Polymers | PP Impact Copolymer | Pinnacle PP |