Boda BDF401HP
| Category: | Fluorelastomer , Fluoroelastomer |
| Manufacturer: | Chenguang Fluoro & Silicone Elastomers Co., Ltd. |
| Trademark: | Boda |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bgwU2e_Boda-BDF401HP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
BDF401HP is a medium viscosity curative incorporated fluoroelastomer copolymer. This grade is well suited for application where good rheological properties and excellent compression set resistance are required. BDF401HP can be compounded to meet the major fluoroelastomer specifications. BDF401HP can be used for compression molding of O-rings and gaskets or extrusion of profiles. It can be mixed using typical fluoroelastomer compounding ingredients. Mixing can be accomplished with two-roll mills or internal mixers. Finished goods can be produced by a variety of rubber processing methods. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.80 | g/cm³ | |
| Mooney Viscosity (ML 1+10, 121°C) | 42 | MU | |
| Fluorine Content | 66 | % | |
| Solubility | LMW Ketones and esters |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| MH 1(177°C) | 2.65 | N·m | |
| ML 2(177°C) | 0.320 | N·m | |
| t'90 3(177°C) | 2.4 | min | |
| ts2 4(177°C) | 1.2 | min |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness 5(Shore A) | 76 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 6(Yield) | 15.0 | MPa | ASTM D412 |
| Tensile Elongation 7(Break) | 200 | % | ASTM D412 |
| Compression Set (200°C, 70 hr) | 16 | % | ASTM D395B |
| Additional Information |
|---|
| Test Compound: Polymer: 100 MT Black (N990): 30 phr MgO: 3 phr Ca(OH)2: 6 phr Curing Condition: Press: 10 min at 170°C Oven: 24 hr at 230°C |
| Note Message | |
|---|---|
| 1 . | MDR2000 Rheometer, 100cpm, 0.5° Arc, 6 minutes |
| 2 . | MDR2000 Rheometer, 100cpm, 0.5° Arc, 6 minutes |
| 3 . | MDR2000 Rheometer, 100cpm, 0.5° Arc, 6 minutes |
| 4 . | MDR2000 Rheometer, 100cpm, 0.5° Arc, 6 minutes |
| 5 . | Press Time: 10 min, Press Temperature: 170°C, Post Cure Time: 24 hr, Post Cure Temperature: 230°C |
| 6 . | Press Time: 10 min, Press Temperature: 170°C, Post Cure Time: 24 hr, Post Cure Temperature: 230°C |
| 7 . | Press Time: 10 min, Press Temperature: 170°C, Post Cure Time: 24 hr, Post Cure Temperature: 230°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEKASTER™ F10G10M | Mando Advanced Materials Co., Ltd. | PBT | TEKASTER™ |
| Sylvin 8200-65 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| NORYL™ 6850C resin | SABIC Innovative Plastics Europe | PPE+PS | NORYL™ |
| GTPO™ 8102 EH-2 | S&E Specialty Polymers, LLC | TPO (POE) | GTPO™ |
| Kumho ABS 750 | Korea Kumho Petrochemical Co., Ltd. | ABS | Kumho ABS |