LNP™ LUBRICOMP™ ZFL31XXC compound
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bgggD8_LNP-LUBRICOMP-ZFL31XXC-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP ZFL31XXC is a compound based on PPE+PS resin containing 5% Glass Fiber, 15% PTFE. Added features of this material include: Wear Resistant Also known as: LNP* LUBRICOMP* Compound ZFL-4031 HP Product reorder name: ZFL31XXC |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- | 1.21 | g/cm³ | |
| -- | 1.20 | g/cm³ | |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.50 to 0.70 | % | |
| Across Flow : 24 hr | 0.60 to 0.80 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.070 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.10 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 4010 | MPa | ASTM D638 |
| -- | 3640 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 60.0 | MPa | ASTM D638 |
| Break | 60.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 3 | 2.9 | % | ASTM D638 |
| Yield | 2.8 | % | ISO 527-2/5 |
| Break 4 | 3.6 | % | ASTM D638 |
| Break | 3.2 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 5 | 3650 | MPa | ASTM D790 |
| -- 6 | 4810 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 89.0 | MPa | ISO 178 |
| Break, 50.0 mm Span 7 | 106 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.40 | ||
| vs. Itself - Static | 0.27 | ||
| Wear Factor - Washer | 101 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 80 | J/m | ASTM D256 |
| 23°C 8 | 7.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 380 | J/m | ASTM D4812 |
| 23°C 9 | 24 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 12.0 | J | ASTM D3763 |
| -- | 2.80 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 136 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 10 | 134 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 127 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 11 | 127 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 6.6E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 6.9E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 277 to 288 | °C | |
| Middle Temperature | 288 to 299 | °C | |
| Front Temperature | 299 to 310 | °C | |
| Processing (Melt) Temp | 299 to 304 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1500-55D TFE 15 | RTP Company | TEEE | RTP |
| Sylvin 8250-65 Natural | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |
| NORYL™ GFN2F resin | SABIC Innovative Plastics | PPE+PS | NORYL™ |
| DURACON® YF-10 | Polyplastics Co., Ltd. | Acetal (POM) Copolymer | DURACON® |
| E-Pos 328 | Epocat Nederland BV | Epoxy | E-Pos |