VICTREX® HT™ G45
| Category: | PEK , Polyether Ketone |
| Manufacturer: | Victrex plc |
| Trademark: | VICTREX® HT™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bggGKO_VICTREX-HT-G45.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
High performance thermoplastic material, unreinforced PolyEtherKetone (PEK), semi crystalline, depth filtered granules for injection moulding, low flow, FDA food contact compliant, colour natural/beige. Applications for high strength and stiffness as well as good ductility at higher temperatures. Chemically resistant to aggressive environments, suitable for sterilisation for medical and food contact applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | ISO 1183 | ||
| -- 1 | 1.26 | g/cm³ | ISO 1183 |
| -- 2 | 1.30 | g/cm³ | ISO 1183 |
| Spiral Flow | 19.0 | cm | Internal method |
| Molding Shrinkage 3 | ISO 294-4 | ||
| Vertical flow direction | 1.2 | % | ISO 294-4 |
| Flow direction | 1.0 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr, 3.20 mm | 0.070 | % | ISO 62 |
| Saturated, 23°C, 3.20mm | 0.60 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 23°C) | 86 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 3700 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 115 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 30 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 4200 | MPa | ISO 178 |
| Flexural Stress | ISO 178 | ||
| 3.5% strain, 23°C | 140 | MPa | ISO 178 |
| 23°C | 185 | MPa | ISO 178 |
| 125°C | 110 | MPa | ISO 178 |
| 175°C | 32.0 | MPa | ISO 178 |
| 275°C | 16.0 | MPa | ISO 178 |
| Compressive Stress | ISO 604 | ||
| 25°C | 140 | MPa | ISO 604 |
| 120°C | 90.0 | MPa | ISO 604 |
| 200°C | 30.0 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 7.0 | kJ/m² | ISO 180/A |
| Unnotched Izod Impact Strength (23°C) | No Break | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 163 | °C | ISO 75-2/Ae |
| Glass Transition Temperature | 152 | °C | ISO 11357-2 |
| Melting Temperature | 373 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : < 152°C | 4.5E-4 | cm/cm/°C | ISO 11359-2 |
| Flow : > 152°C | 7.5E-4 | cm/cm/°C | ISO 11359-2 |
| Lateral : < 152°C | 5.5E-4 | cm/cm/°C | ISO 11359-2 |
| Lateral : > 152°C | 1.3E-3 | cm/cm/°C | ISO 11359-2 |
| Specific Heat (23°C) | 2200 | J/kg/°C | DSC |
| Thermal Conductivity (23°C) | 0.29 | W/m/K | ISO 22007-4 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | IEC 60093 | ||
| 23°C | 1.0E+16 | ohms·cm | IEC 60093 |
| 125°C | 1.0E+15 | ohms·cm | IEC 60093 |
| 275°C | 1.0E+9 | ohms·cm | IEC 60093 |
| Dielectric Strength (2.00 mm) | 23 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 150 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Flammability Index (2.00 mm) | 960 | °C | IEC 60695-2-12 |
| Oxygen Index | ISO 4589-2 | ||
| -- 4 | 24 | % | ISO 4589-2 |
| -- 5 | 35 | % | ISO 4589-2 |
| Toxicity | NES 713 | ||
| CO Content | 0.0740 | NES 713 | |
| CO2 Content | 0.150 | NES 713 | |
| Total Gases | 0.220 | NES 713 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (400°C) | 350 | Pa·s | ISO 11443 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 150 | °C | |
| Drying Time | 3.0 - 5.0 | hr | |
| Hopper Temperature | < 100 | °C | |
| Rear Temperature | 390 | °C | |
| Middle Temperature | 395 - 405 | °C | |
| Front Temperature | 410 | °C | |
| Nozzle Temperature | 415 | °C | |
| Mold Temperature | 200 - 220 | °C |
| Injection instructions |
|---|
| Runner: Die / nozzle >3mm, manifold >3.5mmGate: >1mm or 0.5 x part thickness |
| Note Message | |
|---|---|
| 1 . | Amorphous |
| 2 . | Crystalline |
| 3 . | 415°C nozzle, 220°C tool |
| 4 . | 0.4 mm |
| 5 . | 3.2 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 800 Z | RTP Company | Acetal (POM) Copolymer | RTP |
| Fainplast PVC GS 0145/R | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Lupoy® 1302-07 | LG Chem Ltd. | PC | Lupoy® |
| Petro Rabigh PP FS3011E | Rabigh Refining & Petrochemical Co. | PP Homopolymer | Petro Rabigh PP |
| Plenco 06500 (Transfer) | Plastics Engineering Co. | Phenolic | Plenco |