Braskem PP H502-25RZ

Category:	PP Homopolymer , Polypropylene Homopolymer
Manufacturer:	Braskem Europe GmbH
Trademark:	Braskem PP
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	bgQchh_Braskem-PP-H502-25RZ.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
Braskem H502-25RZ Polypropylene Resin is a homopolymer resin suitable for the use in spunbonded nonwovens production equipment. Braskem H502-25RZ Polypropylene Resin can also be used in other Fiber spinning processes. Braskem H502-25RZ Polypropylene Resin is a controlled rheology polypropylene offering excellent processability at melt temperatures between 220 and 280°C. Applications for Braskem H502-25RZ Polypropylene Resin: Nonwovens for health and hygiene Carpet face yarns Geotextiles Upholstery Filtration Agricultural materials Complies with: EU, No 10/2011 U.S. FDA 21 CFR 177.1520(c)1.1 Consult the regulations for complete details.

Message

Braskem H502-25RZ Polypropylene Resin is a homopolymer resin suitable for the use in spunbonded nonwovens production equipment. Braskem H502-25RZ Polypropylene Resin can also be used in other Fiber spinning processes. Braskem H502-25RZ Polypropylene Resin is a controlled rheology polypropylene offering excellent processability at melt temperatures between 220 and 280°C.

Applications for Braskem H502-25RZ Polypropylene Resin:

Nonwovens for health and hygiene

Carpet face yarns

Geotextiles

Upholstery

Filtration

Agricultural materials

Complies with:

EU, No 10/2011

U.S. FDA 21 CFR 177.1520(c)1.1

Consult the regulations for complete details.

General Information
Agency Ratings	EU No 10/2011 FDA 21 CFR 177.1520(c) 1.1
Forms	Pellets
Processing Method	Fiber (Spinning) Extrusion

Physical	Nominal Value	Unit	Test Method
Density	0.900	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg)	25	g/10 min	ISO 1133

Mechanical	Nominal Value	Unit	Test Method
Tensile Stress (Yield, Injection Molded)	30.0	MPa	ISO 527-2
Tensile Strain (Yield, Injection Molded)	10	%	ISO 527-2
Flexural Modulus (Injection Molded)	1300	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (23°C, Injection Molded)	2.0	kJ/m²	ISO 179/1eA

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (0.45 MPa, Unannealed)	80.0	°C	ISO 75-2/B
Vicat Softening Temperature	148	°C	ISO 306/A

Extrusion	Nominal Value	Unit
Melt Temperature	220 to 280	°C

Resin Grade	Manufacturer	Category	Trademark
Maxelast® P3780	Nantong Polymax Elastomer Technology, Co., Ltd	TPE	Maxelast®
PRL PC-HH-UV	Polymer Resources Ltd.	PC	PRL
ASI POLYETHYLENE LP 551-01	A. Schulman Inc.	HDPE Copolymer	ASI POLYETHYLENE
Hyundai EP Adhesives LE851P/1002	HYUNDAI EP Co., Ltd.	PE, Unspecified	Hyundai EP Adhesives
Paracril® P3380XP	INSA	NBR	Paracril®