Syncure™ System S112BL
| Category: | XLPE , Crosslinked Polyethylene |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Syncure™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bfy0RW_Syncure-System-S112BL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Syncure™ systems are two part moisture crosslinkable compounds. S112BL is a CSA listed, high strength, weather resistant, black (2.5% carbon black) cable insulation compound. RoHS compliant. Graft resin component of this system has approximate shelf life of 6 months from the date of production. Please consult PolyOne for its use past 6 months. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Wire Types |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.933 | g/cm³ | ASTM D792 |
| Gel Content 1 | 72 | % | ASTM D2765 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Resistance 2 | 82.3 | kN/m | ASTM D1004 |
| Aging | Nominal Value | Unit | |
|---|---|---|---|
| Tensile strength retention rate 3(121°C, 1.91 mm) | 95 | % | |
| Elongation retention rate 4(121°C, 1.91 mm) | 90 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deformation 5(131°C) | 7.5 | % | UL 1581 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Catalyst parent mixture- S-1044B 6 | 10 | % | |
| Transplant-based resin- S-1054A 7 | 90 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shaw D | 52 | ASTM D2240 | |
| Shaw D, 10 seconds | 48 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 8(Yield) | 15.9 | MPa | ASTM D638 |
| Tensile Elongation 9(Break) | 500 | % | ASTM D638 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 39 | kV/mm | ASTM D149 |
| Dielectric Constant | 2.45 | ASTM D150 | |
| Dissipation Factor | 2.0E-3 | ASTM D150 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| 存放和搬运：包装打开之后应在48小时之内使用，避免自硬化和报废。 |
| Note Message | |
|---|---|
| 1 . | Cross-linked PE, Method B (Non-Arbitration Test) |
| 2 . | Mold C,2 inches/min |
| 3 . | 336 hours, UL standard |
| 4 . | 336 hours, UL standard |
| 5 . | 500g,1 hour |
| 6 . | S-1044B |
| 7 . | S-1054A |
| 8 . | Type 4, 510mm/min |
| 9 . | Type 4, 510mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Titalon® 2158GCF | Titan Plastics Compounds Co., Ltd. | Nylon 66 | Titalon® |
| Abstron IM-14 S | Bhansali Engineering Polymers Limited | ABS | Abstron |
| ACRYLITE® Resist ZK6SR | Evonik Cyro LLC | Acrylic (PMMA) | ACRYLITE® |
| DJSilicone NE-5140 | DONGJUE SILICONE (NANJING) CO., LTD | Silicone | DJSilicone |
| LUVOCOM® 1301-VAP 10 | LEHVOSS Group | PPS | LUVOCOM® |