Jamplast JPEVA18
| Category: | EVA , Ethylene Vinyl Acetate Copolymer |
| Manufacturer: | Jamplast, Inc. |
| Trademark: | Jamplast |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bf0gwV_Jamplast-JPEVA18.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| JPEVA18 is an EVA copolymer with excellent flexibility and low temperature properties. JPEVA18 is very suitable for medium to heavy gauge film applications as well as injection and blow molding. JPEVA18 contains no additives. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.1 | g/10 min | ASTM D1238 |
| Vinyl Acetate Content | 18.0 | wt% |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 91 | ASTM D2240 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Secant Modulus | ASTM D882 | ||
| 1% Secant, MD | 51.7 | MPa | |
| 1% Secant, TD | 59.3 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield | 4.68 | MPa | |
| TD : Yield | 4.30 | MPa | |
| MD : Break | 41.0 | MPa | |
| TD : Break | 30.3 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break | 410 | % | |
| TD : Break | 560 | % | |
| Dart Drop Impact (38 µm) | 610 | g | ASTM D1709 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -76.1 | °C | ASTM D746 |
| Vicat Softening Temperature | 65.0 | °C | ASTM D1525 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 232 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 9739-90 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| HiFill® PA6 GB20 L | Techmer Engineered Solutions | Nylon 6 | HiFill® |
| Latamid SP1 | LATI S.p.A. | Nylon 610 | Latamid |
| Iupilon® FPR3500 | Mitsubishi Engineering-Plastics Corp | PC | Iupilon® |
| TechnoElast V A8000 I 2 sw | TechnoCompound GmbH | TPE | TechnoElast |