NYLOY® MG-0033N
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Nytex Composites Co., Ltd. |
| Trademark: | NYLOY® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | beurOl_NYLOY-MG-0033N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| NYLOY® MG-0033N is a Polyamide 66 (Nylon 66) material filled with 33% glass fiber. It is available in Asia Pacific or North America for injection molding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.18 | g/cm³ | ASTM D792 |
| -- | 1.38 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ASTM D955, ISO 294-4 | ||
| Flow | 0.43 | % | |
| Across Flow | 1.2 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 115 | ASTM D785, ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| -- | 177 | MPa | ASTM D638 |
| -- | 180 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 2.0 | % | ASTM D638 |
| Break | 3.2 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 10000 | MPa | ASTM D790 |
| -- | 8700 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 265 | MPa | ASTM D790 |
| -- | 270 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 15 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C, 3.18 mm) | 160 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed | 250 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 245 | °C | ISO 75-2/A |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 270 to 300 | °C | |
| Mold Temperature | 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shanghai Potomer SG8 | Shanghai Potomer International Trade Co., Ltd. | PVC, Rigid | Shanghai Potomer |
| Novalloy-E E11 | Daicel Polymer Ltd. | ABS | Novalloy-E |
| Dragon-Skin® 30 | Smooth-On, Inc | Silicone | Dragon-Skin® |
| Edgetek™ PS-30CF/000 HF UV BLACK | PolyOne Corporation | PBT | Edgetek™ |
| PERCOM® WCB70 | A. Schulman Europe | PP Copolymer | PERCOM® |