SABIC® PPcompound 7795
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® PPcompound |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bdtrpG_SABIC-PPcompound-7795.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® PPcompound 7795 is a mineral filled modified polypropylene. This material combines high scratch resistance, good stiffness, high impact and excellent flow. This material has a very broad processing window and good esthical performance. Typical applications include esthetical automotive interior parts such as door panels and interior trim. SABIC® PPcompound 7795 is a designated automotive grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.00 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 30 | g/10 min | ISO 1133 |
| Molding Shrinkage (24 hr) | 0.85 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, Injection Molded) | 66 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/5/50 | ||
| Yield, 3.20 mm, Injection Molded | 24.0 | MPa | |
| Break, 3.20 mm, Injection Molded | 20.0 | MPa | |
| Tensile Strain (Break, 3.20 mm, Injection Molded) | 50 | % | ISO 527-2/5/50 |
| Flexural Modulus 1(Injection Molded) | 1600 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C, Injection Molded) | 40 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact Strength | ISO 180/4A | ||
| -20°C, Injection Molded | 5.0 | kJ/m² | |
| 0°C, Injection Molded | 8.0 | kJ/m² | |
| 23°C, Injection Molded | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 110 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 125 | °C | ISO 306/A |
| CLTE - Flow | ASTM D696 | ||
| -30 to 30°C | 5.7E-5 | cm/cm/°C | |
| 23 to 80°C | 8.5E-5 | cm/cm/°C |
| Note Message | |
|---|---|
| 1 . | Method I (3 point load) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinpolene MBB206 | Teknor Apex Asia Pacific PTE. LTD. | PE, Unspecified | Sinpolene |
| ABSCOM® FR1000 | Polymer Compounders Limited | ABS | ABSCOM® |
| Nypol® PA A3 G30 M2 NTLA014 NR394 MSP | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| K-Bin Rigid PVC KBD-5037T-5 | K-Bin, Inc. | PVC, Rigid | K-Bin Rigid PVC |
| LinGen FR280 | Shanghai Lin Gen Rubber Materials Co., Ltd. | TPE | LinGen |