LNP™ THERMOTUF™ VF1001S compound
| Category: | Nylon, Unspecified , Polyamide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOTUF™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bdqG9F_LNP-THERMOTUF-VF1001S-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOTUF VF1001S is a compound based on Super Tough Nylon resin containing 5% Glass Fiber. Added features of this material include: Heat Stabilized, High Impact. Also known as: LNP* THERMOTUF* Compound VF-1001 HS Product reorder name: VF1001S |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.12 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 1.0 to 3.0 | % | |
| Across Flow : 24 hr | 1.0 to 3.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.68 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 1.1 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 3390 | MPa | ASTM D638 |
| -- | 3300 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 61.8 | MPa | ASTM D638 |
| Yield | 61.0 | MPa | ISO 527-2/5 |
| Break 3 | 56.4 | MPa | ASTM D638 |
| Break | 56.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 3.4 | % | ASTM D638 |
| Yield | 3.5 | % | ISO 527-2/5 |
| Break 5 | 9.4 | % | ASTM D638 |
| Break | 7.6 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 2940 | MPa | ASTM D790 |
| -- 7 | 2760 | MPa | ISO 178 |
| Flexural Stress | 86.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 110 | J/m | ASTM D256 |
| 23°C 8 | 9.5 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 720 | J/m | ASTM D4812 |
| 23°C 9 | 42 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 8.90 | J | ASTM D3763 |
| -- | 11.9 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 249 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 10 | 242 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 198 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 11 | 154 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 6.4E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 9.8E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 260 to 271 | °C | |
| Middle Temperature | 271 to 282 | °C | |
| Front Temperature | 288 to 299 | °C | |
| Processing (Melt) Temp | 271 to 293 | °C | |
| Mold Temperature | 48.9 to 93.3 | °C | |
| Back Pressure | 0.344 to 0.689 | MPa | |
| Screw Speed | 10 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nipol® SBR NS310S | Zeon Corporation | SBR, Solution | Nipol® SBR |
| Hytrel® 4556 | DuPont Performance Polymers | TPC-ET | Hytrel® |
| KumhoSunny PC HCG2520MP | Shanghai KumhoSunny Plastics Co., Ltd. | PC | KumhoSunny PC |
| Pearlthane® ECO D12T90E | Lubrizol Advanced Materials, Inc. | TPU-Polyester | Pearlthane® ECO |
| Polifil® PP RMC-10 | The Plastics Group | PP Impact Copolymer | Polifil® PP |