Generic Nylon 6 - Glass Bead\Glass Fiber
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bdfXQ1_Generic-Nylon-6---Glass-Bead-Glass-Fiber.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic Nylon 6 - Glass Bead\Glass Fiber This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.34 - 1.36 | g/cm³ | ASTM D792 |
| 23°C | 1.34 - 1.37 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.39 - 0.61 | % | ASTM D955 |
| 23°C | 0.28 - 1.3 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 6.5 - 7.1 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 2.0 - 2.3 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 185 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 6110 - 6210 | MPa | ASTM D638 |
| 23°C | 4700 - 8890 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Fracture, 23°C | 116 - 125 | MPa | ASTM D638 |
| Fracture, 23°C | 92.6 - 125 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Fracture, 23°C | 2.0 - 4.0 | % | ASTM D638 |
| Fracture, 23°C | 2.4 - 5.0 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 4770 - 5810 | MPa | ASTM D790 |
| 23°C | 4690 - 5870 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 130 - 200 | MPa | ASTM D790 |
| 23°C | 144 - 186 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.0 - 12 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 34 - 46 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 37 - 61 | J/m | ASTM D256 |
| 23°C | 4.0 - 10 | kJ/m² | ISO 180 |
| Unnotched Izod Impact Strength (23°C) | 30 - 36 | kJ/m² | ISO 180 |
| Multi-Axial Instrumented Impact Energy (23°C) | 2.00 - 3.63 | J | ISO 6603-2 |
| Multi-Axial Instrumented Impact Peak Force (23°C) | 700 - 813 | N | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 200 - 216 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, not annealed | 180 - 204 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 189 - 192 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 199 - 211 | °C | ISO 306 |
| Melting Temperature | |||
| -- | 222 | °C | ISO 11357-3 |
| -- | 220 | °C | ISO 3146 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 3.0E-5 - 3.8E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 9.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+10 - 2.5E+14 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+13 - 2.5E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength (23°C) | 11 - 37 | kV/mm | IEC 60243-1 |
| Relative Permittivity (23°C) | 4.25 | IEC 60250 | |
| Dissipation Factor (23°C) | 0.013 - 0.027 | IEC 60250 | |
| Comparative Tracking Index | 323 - 506 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Flammability Index | 650 - 960 | °C | IEC 60695-2-12 |
| Oxygen Index | 23 - 24 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 80.5 | °C | |
| Drying Time | 2.9 - 5.3 | hr | |
| Suggested Max Moisture | 0.085 - 0.20 | % | |
| Rear Temperature | 235 - 282 | °C | |
| Middle Temperature | 250 - 282 | °C | |
| Front Temperature | 255 - 282 | °C | |
| Processing (Melt) Temp | 245 - 280 | °C | |
| Mold Temperature | 70.0 - 101 | °C |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic Nylon 6 - Glass Bead\Glass FiberThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Taitacell EPS-351Ss | Taita Chemical Company, Ltd. | PS (EPS) | Taitacell |
| Toler PP PP2024 | Toler Chemical, Inc | PP Impact Copolymer | Toler PP |
| CONTINUUM™ DGDA-2490 NT | The Dow Chemical Company | HDPE | CONTINUUM™ |
| CoolPoly® D5506 | Celanese Corporation | LCP | CoolPoly® |
| Sylvin 9077-85 Yellow 4113 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |