CoolPoly® D3608
| Category: | Nylon 46 , Polyamide 46 |
| Manufacturer: | Cool Polymers, Inc. |
| Trademark: | CoolPoly® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bdCunh_CoolPoly-D3608.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| CoolPoly D series of thermally conductive plastics transfers heat, a characteristic previously unavailable in injection molding grade polymers. CoolPoly is lightweight, netshape moldable and allows design freedom in applications previously restricted to metals. The D series is electrically non-conductive and can be used for its dielectric properties. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.70 | g/cm³ | ISO 1183 |
| Water Absorption (Saturation) | 0.50 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 10000 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 86.0 | MPa | ISO 527-2 |
| Nominal Tensile Strain at Break | 1.0 | % | ISO 527-2 |
| Flexural Modulus | 9500 | MPa | ISO 178 |
| Flexural Stress | 120 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 2.8 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 13 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Heat | 1030 | J/kg/°C | ASTM E1461 |
| Thermal Conductivity | 1.6 | W/m/K | ASTM E1461 |
| Thermal Diffusivity | 0.00900 | cm²/s | ASTM E1461 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 104 | °C | |
| Drying Time | 24 | hr | |
| Dew Point | -40.0 | °C | |
| Suggested Max Moisture | > 0.050 | % | |
| Rear Temperature | 280 to 321 | °C | |
| Middle Temperature | 300 to 332 | °C | |
| Front Temperature | 310 to 338 | °C | |
| Nozzle Temperature | 290 to 327 | °C | |
| Processing (Melt) Temp | 310 to 343 | °C | |
| Mold Temperature | 105 to 165 | °C | |
| Injection Pressure | 5.20 to 10.4 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Holding Pressure | 1.70 to 5.20 | MPa | |
| Back Pressure | 0.00 to 0.350 | MPa | |
| Screw Speed | 50 to 150 | rpm | |
| Cushion | 0.00 to 6.35 | mm | |
| Screw Compression Ratio | 2.5:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Di-Pak™ E-4595-3 | Hapco Inc. | TP, Unspecified | Di-Pak™ |
| Geon™ HTX 66311 | PolyOne Corporation | PVC Alloy | Geon™ HTX |
| HANWHA LDPE 5320 | Hanwha Chemical | LDPE | HANWHA LDPE |
| Hifax TRC 103P R299 | LyondellBasell Industries | PP Impact Copolymer | Hifax |
| LNP™ STAT-KON™ FX91304 compound | SABIC Innovative Plastics | PE, Unspecified | LNP™ STAT-KON™ |