Aurora PVC AP4000 Series AAMA
| Category: | PVC, Rigid , Rigid Polyvinyl Chloride |
| Manufacturer: | Aurora Plastics, Inc. |
| Trademark: | Aurora PVC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bbh6Ig_Aurora-PVC-AP4000-Series-AAMA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
A high rate, midrange gloss, PVC pellet, extrusion compound for exterior/interior applications. Typical test results for ASTM D-4216. This is a Rigid PVC formulation per the requirements of AAMA 303-05. Testing was performed on actual window parts with a wall thickness of 0.100". This material meets/exceeds cell class 1-40131-13** as required in ASTM D-4726. Testing was performed by Dallas Laboratory, Inc., March 2007. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.44 to 1.48 | g/cm³ | ASTM D792 |
| PVC Cell Classification | 1-42342-12 | ASTM D4216 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness 1(Shore D, 22°C) | 76 to 82 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (22°C) | 2560 | MPa | ASTM D638 |
| Tensile Strength (Yield, 22°C) | 43.2 | MPa | ASTM D638 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (22°C) | 800 | J/m | ASTM D256 |
| Drop Impact Resistance | ASTM D4226 | ||
| 22°C, Extruded at 380 to 390° F melt temperature 2 | > 107 | J/cm | |
| 22°C, Extruded at 380 to 390° F melt temperature 3 | > 107 | J/cm |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 66.1 | °C | ASTM D648 |
| CLTE - Flow (22°C) | 5.8E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Burning Rate | ASTM D635 | ||
| AEB | 0.00 | ||
| ATB | 0.00 |
| Note Message | |
|---|---|
| 1 . | Instantaneous |
| 2 . | Procedure A |
| 3 . | Procedure B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PPcompound 6614 | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |
| TUFNYL® SXXIC 9P BLACK | SRF Ltd. | Nylon 6 | TUFNYL® |
| KOCETAL® K300EWBBK | Kolon Plastics, Inc. | Acetal (POM) Copolymer | KOCETAL® |
| InnoTooling™ IE-9040 | Innovative Polymers, Inc. | TSU | InnoTooling™ |
| Sylvin 86041-65D Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |