LNP™ LUBRILOY™ R2000 compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRILOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bag1Zd_LNPLUBRILOYR2000compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRILOY R2000 is a compound based on Nylon 66 resin containing Proprietary Lubricant. Added features of this material include: Internally Lubricated. Also known as: LNP* LUBRILOY* Compound R Product reorder name: R2000 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.03 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/2.16 kg) | 15.0 - 20.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hours | 1.8 - 2.2 | % | ASTM D955 |
| Transverse flow : 24 hours | 2.1 - 3.1 | % | ASTM D955 |
| Water Absorption (24 hr, 50% RH) | 0.25 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 53.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 32 | % | ISO 527-2/50 |
| Flexural Modulus 1 | ISO 178 | ||
| -- | 2100 | MPa | ISO 178 |
| 60°C | 800 | MPa | ISO 178 |
| 100°C | 500 | MPa | ISO 178 |
| Flexural Stress | ISO 178 | ||
| -- | 77.0 | MPa | ISO 178 |
| 60°C | 32.0 | MPa | ISO 178 |
| 100°C | 18.0 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| With self-dynamics | 0.36 | ASTM D3702 Modified | |
| With Self-Static | 0.27 | ASTM D3702 Modified | |
| Flexural Strain at Break 2 | ISO 178 | ||
| -- | 7.0 | % | ISO 178 |
| 60°C | 7.0 | % | ISO 178 |
| 100°C | 7.0 | % | ISO 178 |
| Wear Factor - Washer | 50.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 3(23°C) | 7.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 4(23°C) | 140 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5(1.8 MPa, Unannealed, 64.0 mm Span) | 85.0 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 60°C | 7.7E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 60°C | 1.0E-4 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 - 0.25 | % | |
| Rear Temperature | 266 - 277 | °C | |
| Middle Temperature | 282 - 293 | °C | |
| Front Temperature | 293 - 304 | °C | |
| Processing (Melt) Temp | 271 - 282 | °C | |
| Mold Temperature | 82.2 - 93.3 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2 mm/min |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP EMI 2263 | RTP Company | PEEK | RTP |
| TUFLIN™ HSE-7002 NT 7 | The Dow Chemical Company | LLDPE | TUFLIN™ |
| Ferro PP LPP40BD26WH | Ferro Corporation | PP Homopolymer | Ferro PP |
| DOMAMID® 66G25V0AH | DOMO Engineering Plastics SPA | Nylon 66 | DOMAMID® |
| Medalist® MD-17135 XRD1 (PRELIMINARY DATA) | Teknor Apex Company | TPE | Medalist™ |