Generic PEI - Glass Fiber
| Category: | PEI , Polyether Imide |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bZLPyE_Generic-PEI---Glass-Fiber.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PEI - Glass Fiber This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.33 - 1.61 | g/cm³ | ASTM D792 |
| 23°C | 1.34 - 1.63 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (337°C/6.6 kg) | 3.1 - 14 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (360°C/5.0 kg) | 5.00 - 12.2 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.19 - 0.56 | % | ASTM D955 |
| Transverse flow : 23°C | 0.30 - 0.71 | % | ASTM D955 |
| 23°C | 0.10 - 0.61 | % | ISO 294-4 |
| Water Absorption | |||
| 23°C, 24 hr | 0.13 - 0.24 | % | ASTM D570 |
| Saturated, 23°C | 0.79 - 1.0 | % | ISO 62 |
| Equilibrium, 23°C | 0.90 - 1.2 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.22 - 0.60 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (23°C) | 113 - 124 | ASTM D785 | |
| Ball Indentation Hardness | 140 - 170 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 4340 - 11900 | MPa | ASTM D638 |
| 23°C | 4500 - 11600 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 113 - 169 | MPa | ASTM D638 |
| Yield, 23°C | 115 - 171 | MPa | ISO 527-2 |
| Fracture, 23°C | 112 - 181 | MPa | ASTM D638 |
| Fracture, 23°C | 115 - 180 | MPa | ISO 527-2 |
| 23°C | 117 - 188 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Yield, 23°C | 1.7 - 4.1 | % | ASTM D638 |
| Yield, 23°C | 1.9 - 5.0 | % | ISO 527-2 |
| Fracture, 23°C | 1.9 - 6.1 | % | ASTM D638 |
| Fracture, 23°C | 1.9 - 4.1 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 4720 - 12000 | MPa | ASTM D790 |
| 23°C | 4500 - 11700 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 148 - 271 | MPa | ASTM D790 |
| 23°C | 178 - 252 | MPa | ISO 178 |
| Yield, 23°C | 159 - 241 | MPa | ASTM D790 |
| Fracture, 23°C | 191 - 242 | MPa | ASTM D790 |
| Compressive Strength (23°C) | 124 - 214 | MPa | ASTM D695 |
| Coefficient of Friction | 0.24 - 0.52 | ASTM D1894 | |
| Taber Abrasion Resistance (23°C) | 15.0 - 20.4 | mg | ASTM D1044 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 7.0 - 11 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 30 - 40 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 51 - 120 | J/m | ASTM D256 |
| 23°C | 5.0 - 14 | kJ/m² | ISO 180 |
| Unnotched Izod Impact | |||
| 23°C | 420 - 710 | J/m | ASTM D256 |
| 23°C | 30 - 40 | kJ/m² | ISO 180 |
| Reverse Notch Izod Impact (23°C) | 460 | J/m | ASTM D256 |
| Instrumented Dart Impact | |||
| 23°C | 8.00 - 18.0 | J | ASTM D3763 |
| 23°C | 2.64 - 3.70 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 210 - 213 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 207 - 215 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 204 - 213 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 204 - 210 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 210 - 234 | °C | ASTM D1525 |
| -- | 212 - 225 | °C | ISO 306 |
| Linear thermal expansion coefficient | |||
| Flow | 1.9E-5 - 3.6E-5 | cm/cm/°C | ASTM D696 |
| Flow | 1.4E-5 - 4.0E-5 | cm/cm/°C | ASTM E831 |
| Flow | 1.4E-5 - 3.1E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 2.6E-5 - 6.2E-5 | cm/cm/°C | ASTM E831 |
| Lateral | 4.4E-5 - 6.1E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | |||
| 23°C | 0.22 - 0.26 | W/m/K | ASTM C177 |
| 23°C | 0.24 - 0.33 | W/m/K | ISO 8302 |
| RTI Elec | 105 - 180 | °C | UL 746 |
| RTI Imp | 105 - 170 | °C | UL 746 |
| RTI | 105 - 180 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | |||
| -- | 5.0E+5 - 1.0E+17 | ohms | ASTM D257 |
| -- | 9.8E+14 - 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | |||
| 23°C | 1.0E+3 - 1.0E+17 | ohms·cm | ASTM D257 |
| 23°C | 1.0E+15 - 1.2E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | |||
| 23°C | 20 - 31 | kV/mm | ASTM D149 |
| 23°C | 15 - 35 | kV/mm | IEC 60243-1 |
| Dielectric Constant | |||
| 23°C | 3.48 - 3.92 | ASTM D150 | |
| 23°C | 3.24 | IEC 60250 | |
| Dissipation Factor | |||
| 23°C | 1.3E-3 - 5.3E-3 | ASTM D150 | |
| 23°C | 8.0E-4 - 5.6E-3 | IEC 60250 | |
| Comparative Tracking Index | 100 - 150 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | |||
| -- | 47 - 54 | % | ASTM D2863 |
| -- | 46 - 48 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 - 150 | °C | |
| Drying Time | 3.9 - 5.1 | hr | |
| Drying Time, Maximum | 24 | hr | |
| Dew Point | -28.9 | °C | |
| Hopper Temperature | 90.0 - 100 | °C | |
| Rear Temperature | 348 - 376 | °C | |
| Middle Temperature | 359 - 369 | °C | |
| Front Temperature | 370 - 378 | °C | |
| Nozzle Temperature | 370 - 372 | °C | |
| Processing (Melt) Temp | 363 - 391 | °C | |
| Mold Temperature | 135 - 161 | °C | |
| Injection Pressure | 103 - 121 | MPa | |
| Back Pressure | 0.513 - 0.521 | MPa | |
| Screw Speed | 55 - 80 | rpm | |
| Clamp Tonnage | 8.9 - 9.0 | kN/cm² | |
| Vent Depth | 0.051 | mm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PEI - Glass FiberThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| LNP™ LUBRICOMP™ DFL36 compound | SABIC Innovative Plastics | PC | LNP™ LUBRICOMP™ |
| Plasmer 2080B/8901 | HYUNDAI EP Co., Ltd. | TPE | Plasmer |
| Geon™ CPVC Geon™ CPVC LC110 | PolyOne Corporation | CPVC | Geon™ CPVC |
| POCAN® B 3235 XF 000000 | LANXESS GmbH | PBT | POCAN® |
| LNP™ STAT-KON™ Lexan_LCF1506 compound | SABIC Innovative Plastics | PC | LNP™ STAT-KON™ |