45% Glass Reinforced PET |
General Information | |
---|---|
Filler / Reinforcement |
|
Processing Method |
|
Physical | Nominal Value | Unit | Test Method |
---|---|---|---|
Specific Gravity | 1.70 | g/cm³ | ASTM D792 |
Mechanical | Nominal Value | Unit | Test Method |
---|---|---|---|
Tensile Strength (Yield, 23°C) | 179 | MPa | ASTM D638 |
Tensile Elongation (Break) | 3.0 | % | ASTM D638 |
Flexural Modulus | 15200 | MPa | ASTM D790 |
Flexural Strength | 276 | MPa | ASTM D790 |
Impact | Nominal Value | Unit | Test Method |
---|---|---|---|
Notched Izod Impact (23°C, 3.18 mm) | 120 | J/m | ASTM D256 |
Thermal | Nominal Value | Unit | Test Method |
---|---|---|---|
Deflection Temperature Under Load (0.45 MPa, Unannealed, 3.18 mm) | 247 | °C | ASTM D648 |
Flammability | Nominal Value | Test Method | |
---|---|---|---|
Flame Rating (3.18 mm) | HB | Internal Method |
Injection | Nominal Value | Unit | |
---|---|---|---|
Drying Temperature | 121 | °C | |
Drying Time | 3.0 to 4.0 | hr | |
Suggested Max Moisture | 0.020 | % | |
Rear Temperature | 271 to 293 | °C | |
Middle Temperature | 271 to 293 | °C | |
Front Temperature | 271 to 304 | °C | |
Nozzle Temperature | 271 to 304 | °C | |
Processing (Melt) Temp | 271 to 304 | °C | |
Mold Temperature | 82.2 to 121 | °C | |
Back Pressure | 0.345 | MPa |
Resin Grade | Manufacturer | Category | Trademark |
---|---|---|---|
VENYL UG307 - 8139 | AD majoris | Nylon 66 | VENYL |
VITAMIDE® BI12BK6523 | Jackdaw Polymers | Nylon 6 | VITAMIDE® |
NANTEX® 237DX1 | Nantex Industry Co., Ltd. | SBR, Unspecified | NANTEX® |
AKROLOY® PA GF 30 natural (3177) | AKRO-PLASTIC GmbH | Nylon 66+Nylon 6I/6T | AKROLOY® |
FLEXITEQ™ F95A590 | Marplex Australia Pty. Ltd. | TPV | FLEXITEQ™ |