Next ABS SX-02ABK
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Next Polymers Ltd. |
| Trademark: | Next ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bYrYgX_Next-ABS-SX-02ABK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description ABS Un Filled Black Compound Product Applications Typical application such as computer monitor,Printer,Photocopying machine,calculators ,Battries,Lighting diffusers, Auto exterior parts etc Benefits Good low Temperature Toughness, High gloss & weather resistance |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/5.0 kg) | 15 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.60 | % | |
| Across Flow | 0.60 | % | |
| Water Absorption | ASTM D570 | ||
| 23°C, 24 hr | 0.30 | % | |
| Saturation 1 | 0.70 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 95 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2000 | MPa | ASTM D638 |
| Tensile Strength | 35.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 15 | % | ASTM D638 |
| Flexural Modulus | 2100 | MPa | ASTM D790 |
| Flexural Strength | 70.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 160 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 110 | °C | |
| 1.8 MPa, Unannealed | 92.0 | °C | |
| Vicat Softening Temperature | 105 | °C | ASTM D1525 |
| RTI Elec | 60.0 | °C | UL 746 |
| RTI Imp | 60.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 18 | kV/mm | ASTM D149 |
| Arc Resistance | 160 | sec | ASTM D495 |
| Arc Resistance | PLC 5 | ASTM D495 | |
| Comparative Tracking Index (CTI) | > 550 | V | UL 746 |
| Comparative Tracking Index (CTI) | PLC 0 | UL 746 | |
| Hot-wire Ignition (HWI) | 22 | sec | UL 746 |
| Hot-wire Ignition (HWI) | PLC 3 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature - Hot Air Dryer | 70.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 210 to 220 | °C | |
| Middle Temperature | 220 to 230 | °C | |
| Front Temperature | 230 to 240 | °C | |
| Mold Temperature | 45.0 to 65.0 | °C |
| Note Message | |
|---|---|
| 1 . | Immersed |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Solarkote® A200 | Altuglas International of Arkema Inc. | Acrylic (PMMA) | Solarkote® |
| TAIRIPRO T1202 | Formosa Plastics Corporation | PP Homopolymer | TAIRIPRO |
| Adell PP EQ-14 | Adell Plastics, Inc. | PP Homopolymer | Adell PP |
| LNP™ LUBRICOMP™ ZFL31XXC compound | SABIC Innovative Plastics | PPE+PS | LNP™ LUBRICOMP™ |
| Sylvin 9048-65 CLEAR | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |