SABIC® HDPE M30053S
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® HDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bYctVu_SABIC-HDPE-M30053S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC®HDPE M30053S is a high density polyethylene product,. It can be processed by injection molding and is available in Europe. SABIC®The application fields of HDPE M30053S include container and food contact applications. Features include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.952 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 3.5 | g/10 min | ISO 1133 |
| 190°C/5.0 kg | 10 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 15 sec, Compression Molded) | 61 | ISO 868 | |
| Ball Indentation Hardness (H 132/30) | 45.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (2.00 mm, Compression Molded) | 1020 | MPa | ISO 527-2/1BA/1 |
| Tensile Stress | ISO 527-2/1BA/50 | ||
| Yield, 2.00mm, molded | 24.0 | MPa | ISO 527-2/1BA/50 |
| Fracture, 2.00mm, molded | 33.0 | MPa | ISO 527-2/1BA/50 |
| Tensile Strain (Break, 2.00 mm, Compression Molded) | 2000 | % | ISO 527-2/1BA/50 |
| Tensile Creep Modulus | ISO 899-1 | ||
| 1 hr | 425 | MPa | ISO 899-1 |
| 1000 hr | 225 | MPa | ISO 899-1 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180/1A | ||
| -30°C | 4.7 | kJ/m² | ISO 180/1A |
| 23°C | 5.8 | kJ/m² | ISO 180/1A |
| Tensile Impact Strength | 42.0 | kJ/m² | ISO 8256/1B |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 71.0 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 43.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 125 | °C | ISO 306/A50 |
| -- | 70.0 | °C | ISO 306/B50 |
| Additional Information |
|---|
| Strain at Break, ISO 527, Compression Molded, Type 1BA, 50mm/min, 2mm: >2000%ESCR, SABIC Method, Determined in Rhodacal-DS10 at 60°C, 2 N/mm², thickness 3mm: 100hrTensile Impact Elongation at Break, ISO 8256, Type 1, Method B: 1.6%Tensile Impact Maximum Tension, ISO 8256, Type 1, Method B: 36 MPaMelting Point, DIN 53765, Tmelt(top) at 5°C/min: 132°CEnthalpy Change, DIN 53765: 203J/g |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Precision Polymer Z73B | Precision Polymer Engineering Ltd. | NBR | Precision Polymer |
| TYNEP® P5308 | Tyne Plastics LLC. | PC+PBT | TYNEP® |
| APEX® 65016 | Teknor Apex Company | PVC, Flexible | APEX® |
| LUVOCOM® 50-8479/BL-1 | Lehmann & Voss & Co. | PC | LUVOCOM® |
| Sylvin 6920X08 White 1490 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |