DENITER C 1510
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | Vamp Tech |
| Trademark: | DENITER |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bYUK96_DENITER-C-1510.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PC / PBT, 15% glass fiber reinforced, not Flame Retardant compound, good mechanical properties. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.33 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.40 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4500 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 90.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.0 | % | ASTM D638 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 10 | kJ/m² | ISO 180/A |
| Unnotched Izod Impact Strength | 50 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 110 | °C | ASTM D648A |
| Vicat Softening Temperature | 160 | °C | ASTM D1525 1 |
| RTI Elec | 110 | °C | UL 746 |
| RTI Imp | 110 | °C | UL 746 |
| RTI Str | 110 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (CTI) | 250 | V | UL 746 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 250 | °C | |
| Mold Temperature | 70.0 | °C |
| Note Message | |
|---|---|
| 1 . | Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYLAN AX4100 | POLYMA Kunststoff GmbH & Co. KG | ABS | POLYLAN |
| Rubber Glass® II | Smooth-On, Inc | Silicone | Rubber Glass® |
| Moplen EP200S | PolyMirae | TPU, Unspecified | Moplen |
| Evolue™ SP0540 | Prime Polymer Co., Ltd. | LLDPE | Evolue™ |
| Karina RED COLOR CONCENTRATE 42/6-FC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |