INEOS LDPE M23N430

Category:	EMAA , Ethylene Methacrylic Acid
Manufacturer:	INEOS Olefins & Polymers Europe
Trademark:	INEOS LDPE
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	bXwG0n_INEOS-LDPE-M23N430.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

LDPE extrusion coating product

Applications:
M23N430 is a speciality extrusion coating resin with improved adhesion characteristics. With this grade higher line speeds or lower coating weights are possible compared to standard LDPE grades and to M21N430. Main extrusion coating application fields include aluminium foil and metallised film both for industrial use, food and flexible packaging.

Benefits and Features:
M23N430 is an additive free ethylene-methylacrylic acid copolymer (EMMA) with a medium MAA content. Its special polymer structure gives the following properties:

Adhesive properties superior to standard LDPE and to low acid copolymer extrusion coating grades especially with aluminium foil and metallised film at high line speeds or low coating weights

Good processability in mono- and coextrusion with comparable neck in and draw down to LDPE grades

Low fumes during extrusion

Good organoleptical properties

Good heat sealing properties enhanced by the presence of comonomer

High purity and very low gel level

General Information
Features	Additive Free Fast Molding Cycle Good Adhesion Good Heat Seal Good Organoleptic Properties Good Processability High Purity Low Gel Low to No Fumes
Uses	Foil Coatings Food Packaging Packaging Thin Coatings
RoHS Compliance	Contact Manufacturer
Processing Method	Coextrusion Extrusion Coating

Physical	Nominal Value	Unit	Test Method
Density ¹	0.923	g/cm³	ISO 1183/D
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	7.5	g/10 min	ISO 1133
Methacrylic Acid Content	2.5	%	Internal Method

Hardness	Nominal Value	Unit	Test Method
Shore Hardness (Shore D, Compression Molded)	48		ISO 868

Mechanical	Nominal Value	Unit	Test Method
Tensile Stress			ISO 527-2
Yield, Compression Molded	9.50	MPa
Break, Compression Molded	10.5	MPa
Tensile Strain (Break, Compression Molded)	500	%	ISO 527-2

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	90.0	°C	ISO 306/A
Melting Temperature	108	°C	Internal Method

Extrusion	Nominal Value	Unit
Melt Temperature	280 to 325	°C

Note Message
1 .	Conditioned according to ISO 1872/1

Resin Grade	Manufacturer	Category	Trademark
Menzolit® BMC 0150	Menzolit Ltd (UK)	Polyester, TS	Menzolit®
SUMILITE® PVC VSL-4501	Sumitomo Bakelite Co., Ltd.	PVDC	SUMILITE® PVC
Chemiton CSF0NA 90	Franplast S.r.l.	SEBS	Chemiton
Daelim Po1y® LD-05	DAELIM INDUSTRIAL CO., LTD.	LDPE	Daelim Po1y®
Petrothene® XL07420B	LyondellBasell Industries	Polyolefin, Unspecified	Petrothene®