CALP 4650GF
| Category: | Polyolefin, Unspecified , Polyolefin |
| Manufacturer: | Lion Idemitsu Composites Co., Ltd. |
| Trademark: | CALP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bXgR2Q_CALP-4650GF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| CALP 4650GF is a Polyolefin product filled with glass fiber. It can be processed by injection molding and is available in Asia Pacific. Primary characteristic: food contact acceptable. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.09 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 5.9 | g/10 min | ASTM D1238 |
| Molding Shrinkage | Internal Method | ||
| Flow : 2.00 mm | 1.1 | % | |
| Across Flow : 2.00 mm | 1.2 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 102 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 41.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 13 | % | ASTM D638 |
| Flexural Modulus | 3190 | MPa | ASTM D790 |
| Flexural Strength | 60.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (Area) (23°C) | 3.00 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 154 | °C | ASTM D648 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Melthene® -H S102C | TOSOH Corporation | EVA | Melthene® -H |
| Adell Polyamide AR-39 | Adell Plastics, Inc. | Nylon 66 | Adell Polyamide |
| Borealis PP ZC135 | Borealis AG | TPO | Borealis PP |
| Electrafil® J-3/CF/40 | Techmer Engineered Solutions | Nylon 6 | Electrafil® |
| ESENTTIA 03H82NA-TAR | Polipropileno del Caribe S.A. | PP Homopolymer | ESENTTIA |