TIPPLEN® H 650 F
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | MOL Petrochemicals Co. Ltd. |
| Trademark: | TIPPLEN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bXcgsQ_TIPPLEN-H-650-F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TIPPLEN H 650 F is a homopolymer polypropylene for the production of biaxially oriented films designed for high speed production. The grade does not contain any slip or antiblocking agents. The grade has low ash content. TIPPLEN H 650 F is Ca-stearate free and it is particularly suitable for metallization both in monolayer and in coextruded structures. BOPP films made from TIPPLEN H 650 F have good mechanical properties, high impact strength and puncture resistance even at low temperatures. The BOPP film forms an excellent barrier against moisture, oils and oxidation and features good optical properties. Monolayer or coextruded films with a thickness range of 0.01 - 0.04 mm are used for packaging. TIPPLEN H 650 F is suitable for food contact. The product complies with Food Contact Regulations. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 3.0 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 100 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Injection Molded) | 1600 | MPa | ISO 527-2 |
| Tensile Stress (Yield, Injection Molded) | 35.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield, Injection Molded) | 9.5 | % | ISO 527-2 |
| Flexural Modulus (Injection Molded) | 1700 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C, Injection Molded) | 6.0 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 105 | °C | ISO 75-2/B |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 190 to 240 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mirakutoran® TPU E670MNAT | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| Adsyl 5 C 33 F | LyondellBasell Industries | Polyolefin, Unspecified | Adsyl |
| Golden Compound PP S²PC 3545 BO GF20 | Golden Compound GmbH | PP, Unspecified | Golden Compound |
| Hifax EYC 361P G13063 | LyondellBasell Industries | PP Copolymer | Hifax |
| POCAN® B 2505 000000 | LANXESS GmbH | PBT | POCAN® |