GETILAN GPE/400 G
| Category: | XLPE , Crosslinked Polyethylene |
| Manufacturer: | Crosspolimeri S.p.A. |
| Trademark: | GETILAN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bXVxDM_GETILAN-GPE-400-G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
GETILAN is the trade-mark of our crosslinkable polythene. GETILAN GPE/400 G is a medium density chemically crosslinkable compound for power insulation, suitable also for G7. It is a conveniently grafted polythene able to react in presence of moisture and of a catalyst. Normally we suggest our catalyst type MAC/202 or MAC/203 (suitable for extrusioin temperature lower than 215/220°C) REACTION BETWEEN GRAFTING AND CATALYST: These two polythenes, separately stored, must be mixed before starting extrusion in the ratio: GRAFTING/CATALYST 94/6 Certify : IEC 60502-1 XLPE, EPR/HEPR,CEI 2011 G7,HD 22-1 EI7 |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.925 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/5.0 kg) | 0.20 - 0.60 | g/10 min | ASTM D1238 |
| Water absorption rate- 24 hr (70°C) | g/m² | IEC 60811 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset 1 | IEC 60811 | ||
| 250°C | 30 | % | IEC 60811 |
| Residual : 250°C | -5.0 | % | IEC 60811 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Head Temperature | 210 | °C |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 18.0 | MPa | IEC 60811 |
| Tensile Strain (Break) | 360 | % | IEC 60811 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air | IEC 60811 | ||
| 127°C, 40 hr | 9.0 | % | IEC 60811 |
| 150°C, 168 hr | 5.0 | % | IEC 60811 |
| Change in Tensile Strain at Break in Air | IEC 60811 | ||
| 127°C, 40 hr | -3.0 | % | IEC 60811 |
| 150°C, 168 hr | -2.0 | % | IEC 60811 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | BS 6622 |
| Additional Information |
|---|
| CROSSLINKING:Crosslinking of the finished product is obtained by: Immersion of the bobbin into hot water at 85/90°C for two hours (up to 3 mm thickness). Steam treatment at 0.15 for bar 5/6 hours. Faster ambient curing is possible depending from the atmospheric conditions. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 160 | °C | |
| Cylinder Zone 2 Temp. | 175 | °C | |
| Cylinder Zone 3 Temp. | 190 | °C | |
| Cylinder Zone 4 Temp. | 200 | °C | |
| Die Temperature | 225 | °C |
| Note Message | |
|---|---|
| 1 . | 20 N/cm² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 405 HI | RTP Company | PS (HIPS) | RTP |
| RTP 301 FR | RTP Company | PC | RTP |
| NEFTEKHIM PS 945E | Nizhnekamskneftekhim Inc. | PS (HIPS) | NEFTEKHIM PS |
| FHR Polypropylene 23S2A | Flint Hills Resources, LP | PP Random Copolymer | FHR Polypropylene |
| LNP™ STAT-KON™ DD200C compound | SABIC Innovative Plastics Asia Pacific | PC | LNP™ STAT-KON™ |