Lustran® ABS 1152
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | INEOS ABS (USA) |
| Trademark: | Lustran® ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bXV86S_Lustran-ABS-1152.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Lustran ABS 1152 resin is a very high-impact extrusion grade of ABS (acrylonitrile butadiene styrene) with a balance of properties not offered by other grades of ABS. It offers superior toughness, particularly for low-temperature applications, and good thermoformability. It is easy to color with ABS color concentrates. Lustran ABS 1152 resin is used in extrusion applications where super toughness is a prime consideration. Typical applications include vehicle instrument panels, luggage shells, agricultural equipment, and construction equipment. It is also used as a substrate under other specialty grade, such as Lustran ABS 556 low gloss resin and Centrex® weatherable polymers. As with any product, use of Lustran ABS 1152 resin in a given application must be tested (including but not limited to field testing) in advance by the user to determine suitability. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.03 | g/cm³ | ASTM D792 |
| Specific Volume | 0.970 | cm³/g | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/10.0 kg) | 7.3 | g/10 min | ASTM D1238 |
| Water Absorption 1(23°C, 24 hr) | 0.40 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 93 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ASTM D638 | ||
| -18°C | 2210 | MPa | ASTM D638 |
| 23°C | 1520 | MPa | ASTM D638 |
| 71°C | 1240 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield, -18°C | 40.7 | MPa | ASTM D638 |
| Yield, 23°C | 31.0 | MPa | ASTM D638 |
| Yield, 71°C | 19.3 | MPa | ASTM D638 |
| Flexural Modulus | ASTM D790 | ||
| -40°C | 2000 | MPa | ASTM D790 |
| 23°C | 1790 | MPa | ASTM D790 |
| 71°C | 1380 | MPa | ASTM D790 |
| Flexural Strength | ASTM D790 | ||
| Yield, -40°C | 80.7 | MPa | ASTM D790 |
| Yield, 23°C | 48.3 | MPa | ASTM D790 |
| Yield, 71°C | 32.4 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C, 3.18 mm | 220 | J/m | ASTM D256 |
| -18°C, 3.18 mm | 350 | J/m | ASTM D256 |
| 23°C, 3.18 mm | 490 | J/m | ASTM D256 |
| Instrumented Dart Impact 2 | ASTM D3763 | ||
| -40°C, Peak Energy 3 | 31.2 | J | ASTM D3763 |
| -40°C, Total Energy 4 | 35.3 | J | ASTM D3763 |
| -18°C, Peak Energy 5 | 33.9 | J | ASTM D3763 |
| -18°C, Total Energy 6 | 47.5 | J | ASTM D3763 |
| 23°C, Peak Energy 7 | 29.8 | J | ASTM D3763 |
| 23°C, Total Energy 8 | 50.2 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 89.4 | °C | ASTM D648 |
| 0.45 MPa, annealed | 96.7 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 82.2 | °C | ASTM D648 |
| 1.8 MPa, annealed | 90.6 | °C | ASTM D648 |
| CLTE - Flow | 1.0E-4 | cm/cm/°C | ASTM D696 |
| RTI Elec (1.50 mm) | 60.0 | °C | UL 746 |
| RTI Imp (1.50 mm) | 60.0 | °C | UL 746 |
| RTI (1.50 mm) | 60.0 | °C | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate 9(3.18 mm) | 36 | mm/min | ASTM D635 |
| Flame Rating (1.50 mm) | HB | UL 94 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gardner Gloss (60 °, extruded sheet) | 80 | ASTM D523 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 - 93.3 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Suggested Max Moisture | < 0.030 | % | |
| Cylinder Zone 1 Temp. | 216 - 241 | °C | |
| Cylinder Zone 2 Temp. | 216 - 241 | °C | |
| Cylinder Zone 3 Temp. | 216 - 241 | °C | |
| Cylinder Zone 4 Temp. | 216 - 241 | °C | |
| Cylinder Zone 5 Temp. | 216 - 241 | °C | |
| Melt Temperature | 216 - 249 | °C | |
| Die Temperature | 210 - 241 | °C | |
| Take-Off Roll | 62.8 - 104 | °C |
| Extrusion instructions |
|---|
| Max Regrind Allowed: 40% |
| Note Message | |
|---|---|
| 1 . | Injection Molded specimen |
| 2 . | 0.5 in dart, 3 in clamp |
| 3 . | 3.40 m/sec |
| 4 . | 3.40 m/sec |
| 5 . | 2.32 m/sec |
| 6 . | 3.40 m/sec |
| 7 . | 3.40 m/sec |
| 8 . | 3.40 m/sec |
| 9 . | Injection Molded specimen |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SWANCOR Epoxy 978 | SWANCOR IND. CO., LTD. | Epoxy | SWANCOR Epoxy |
| Anjacom® 350-GK30 | Almaak International GmbH | Nylon 66 | Anjacom® |
| Gallonprene® GP210-5011 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| DynaStat® 2257 | Polymer Dynamix | Nylon 12 | DynaStat® |
| Hostalen PP H5416 K | LyondellBasell Industries | PP Random Copolymer | Hostalen |