DIC.PPS FZL-4033
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | DIC Corporation |
| Trademark: | DIC.PPS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bWiLtG_DIC-PPS-FZL-4033.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.68 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.25 | % | |
| Across Flow | 1.2 | % | |
| Water Absorption (23°C, 24 hr) | 0.020 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| M-Scale | 98 | ||
| R-Scale | 118 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 10000 | MPa | ASTM D638 |
| Tensile Strength | 150 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.6 | % | ASTM D638 |
| Flexural Modulus | 9000 | MPa | ASTM D790 |
| Flexural Strength | 230 | MPa | ASTM D790 |
| Compressive Strength | 180 | MPa | ASTM D695 |
| Poisson's Ratio | 0.36 | ||
| Coefficient of Friction 1 | ASTM D1894 | ||
| vs. Steel - Dynamic | 0.22 | ||
| vs. Steel - Static | 0.22 | ||
| Flexural Elongation at Break | 2.1 | % | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 75 | J/m | ASTM D256 |
| Unnotched Izod Impact | 400 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 265 | °C | ASTM D648 |
| CLTE | ASTM D696 | ||
| Flow : -30 to 90°C | 2.3E-5 | cm/cm/°C | |
| Transverse : -30 to 90°C | 2.3E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength (1.60 mm) | 16 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 4.00 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 2.0E-3 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 290 to 320 | °C | |
| Middle Temperature | 290 to 320 | °C | |
| Front Temperature | 290 to 320 | °C | |
| Mold Temperature | 120 to 150 | °C |
| Note Message | |
|---|---|
| 1 . | P=150KPa, V=0.3m/s |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Exxtral™ Performance Polyolefin CMW203 | ExxonMobil Chemical | TPO | Exxtral™ Performance Polyolefin |
| Kepital® F20-52 | Korea Engineering Plastics Co., Ltd | Acetal (POM) Copolymer | Kepital® |
| Ipethene® 322 | Carmel Olefins Ltd. | LDPE | Ipethene® |
| LubX® C pressed | Röchling Engineering Plastics SE & Co. KG | UHMWPE | LubX® |
| Sumikon® PM-3027 | SBHPP | Phenolic | Sumikon® |