RTP 100 HF UV
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bW6gSV_RTP-100-HF-UV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High Flow - UV Stabilized |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.910 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 1.0 to 2.0 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1380 | MPa | ASTM D638 |
| Tensile Strength | 29.6 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | > 10 | % | ASTM D638 |
| Flexural Modulus | 1380 | MPa | ASTM D790 |
| Flexural Strength | 41.4 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 27 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | 1100 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 54.4 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+14 to 1.0E+16 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm, ** Values per RTP Company testing.) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 191 to 232 | °C | |
| Mold Temperature | 32.2 to 65.6 | °C | |
| Injection Pressure | 68.9 to 103 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ming Dih EPS LS3 | Ming Dih Group Corporation | PS (EPS) | Ming Dih EPS |
| Sup-tech A9000 | Shanghai Suptech Engineering Plastics Co. Ltd. | Nylon 66 | Sup-tech |
| YUNGSOX® PP 2100M | Formosa Polypropylene | PP Homopolymer | YUNGSOX® PP |
| INEOS PP 100-GA09 | INEOS Olefins & Polymers Europe | PP Homopolymer | INEOS PP |
| LubriOne™ AT-000/18T-2S BLK | PolyOne Corporation | Acetal (POM) Copolymer | LubriOne™ |