LUBEMID A26 GK50 NATURAL
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | LUBEN PLAST srl |
| Trademark: | LUBEMID |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bVkwv0_LUBEMID-A26-GK50-NATURAL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Compound based on PA6,6 first choice natural colour. With glass beads 50%. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.53 to 1.57 | g/cm³ | ISO 1183/A |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4000 to 4500 | MPa | ISO 527-2/1A/1 |
| Tensile Stress | ISO 527-2/1A/5 | ||
| Yield | 60.0 to 70.0 | MPa | |
| Break | 55.0 to 65.0 | MPa | |
| Tensile Strain | ISO 527-2/1A/5 | ||
| Yield | 2.0 to 3.0 | % | |
| Break | 4.0 to 5.0 | % | |
| Flexural Modulus 1 | 3000 to 4000 | MPa | ISO 178 |
| Flexural Stress 2 | 105 to 115 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.5 to 4.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 35 to 45 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | |||
| 23°C, 3.20 mm | 50 to 60 | J/m | ASTM D256A |
| 23°C 3 | 40 to 50 | kJ/m² | ASTM D256 |
| 23°C | 3.5 to 4.5 | kJ/m² | ISO 180/A |
| 23°C 4 | 5.0 to 6.0 | kJ/m² | ASTM D256 |
| Unnotched Izod Impact Strength (23°C) | 35 to 45 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 235 to 245 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 230 to 240 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 3.20 mm | 70.0 to 80.0 | °C | ASTM D648 |
| Vicat Softening Temperature | |||
| -- | 240 to 250 | °C | ISO 306/A120 |
| -- | 230 to 240 | °C | ISO 306/B120 |
| Melting Temperature | 250 to 265 | °C | Internal Method |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | Notch E |
| 4 . | Notch A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Geon™ Bold L5800 | PolyOne Corporation | PVC Alloy | Geon™ Bold |
| LTP ZW-3650 | Chengdu Letian Plastics Co., Ltd | PPS Alloy | LTP |
| Rotuba CAB B908 (13% Plasticizer) | Rotuba Extruders, Inc. | CAB | Rotuba CAB |
| SEQUEL® 1480 PUV NATRL | LyondellBasell Industries | TPO (POE) | SEQUEL® |
| SCHULABLEND® (ABS/PA) M/MK 6101 GF8 U | A. Schulman Europe | ABS+Nylon | SCHULABLEND® |