| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | DESCO Co., Ltd. |
| Trademark: | DESOX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bVX2NY_DESOX-DSC402SG2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Descriptions: DESOX™ DSC402SG2 is one of the brands which made by PBT(Poly Butylene Terephthalate) that is filled Glass Fiber & impact resistance substance and reinforced goods. It provides good electric property and mechanical property. Applications: DESOX™ DSC402SG2 is one of the most-used resin requested for electric property and hinge property goods, such as parts of connector, etc. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.40 - 0.60 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 117 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 68.6 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 5.0 | % | ASTM D638 |
| Flexural Modulus | 2940 | MPa | ASTM D790 |
| Flexural Strength | 118 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 69 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 200 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 190 | °C | ASTM D648 |
| Melting Temperature | 222 | °C | DSC |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 140 | °C | |
| Drying Time | 2.0 - 5.0 | hr | |
| Suggested Max Moisture | < 0.20 | % | |
| Rear Temperature | 240 - 250 | °C | |
| Middle Temperature | 240 - 255 | °C | |
| Front Temperature | 240 - 260 | °C | |
| Nozzle Temperature | 240 - 260 | °C | |
| Processing (Melt) Temp | 240 - 260 | °C | |
| Mold Temperature | 50.0 - 100 | °C |
| Injection instructions |
|---|
| Speed: 40 to 70%Pressure 1st: 30 to 60%Pressure 2nd: 30 to 60Holding Pressure: 10 to 20% |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ranger PBT PBT-403-M-G10 HF | Beijing Ranger Chemical Co., Ltd. | PBT | Ranger PBT |
| Toraycon® 1100M | Toray Plastics (Malaysia) Sdn. Bhd. | PBT | Toraycon® |
| Niche PA6GF13N | Niche Polymer, LLC | Nylon 6 | Niche |
| MAJORIS CETAL DG330 | AD majoris | Acetal (POM) Copolymer | MAJORIS |
| PLUSTEK PB847I4 | Polyram Ram-On Industries | Nylon 6 | PLUSTEK |