Leona™ TR382
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Asahi Kasei Chemicals Corporation |
| Trademark: | Leona™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bVOPa6_Leona-TR382.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Leona™ TR382 is a Polyamide 66 (Nylon 66) product. It is available in Africa & Middle East, Asia Pacific, Europe, or North America. Applications of Leona™ TR382 include automotive, electrical/electronic applications, engineering/industrial parts and wire & cable. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.08 | -- | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage - Flow | 1.7 to 2.5 | -- | % | Internal Method |
| Water Absorption | ||||
| Saturation, 23°C | -- | 1.7 | % | |
| Equilibrium, 23°C, 50% RH | -- | 1.7 | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 107 | 89 | ASTM D785, ISO 2039-2 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 1900 | 700 | MPa | ISO 527-2 |
| Tensile Stress | ||||
| Yield, 23°C | 53.0 | 35.0 | MPa | ISO 527-2 |
| Break, 23°C | 45.0 | -- | MPa | ISO 527-2 |
| -- | 54.0 | 37.0 | MPa | ASTM D638 |
| Tensile Strain | ||||
| Yield, 23°C | 5.5 | 28 | % | ISO 527-2 |
| Break | 70 | 220 | % | ASTM D638 |
| Break, 23°C | 60 | > 100 | % | ISO 527-2 |
| Flexural Modulus | ||||
| -- | 2000 | 1000 | MPa | ASTM D790 |
| 23°C | 2000 | 700 | MPa | ISO 178 |
| Flexural Strength | ||||
| -- | 79.0 | 39.0 | MPa | ASTM D790 |
| 23°C | 73.0 | 30.0 | MPa | ISO 178 |
| Taber Abrasion Resistance (1000 Cycles) | -- | 6.00 | mg | ASTM D1044 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 80 kJ/m² | No Break | ISO 179 | |
| Charpy Unnotched Impact Strength | No Break | No Break | ISO 179 | |
| Notched Izod Impact | 1100 | 1300 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ||||
| 0.45 MPa, Unannealed | 215 | -- | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 183 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 73.0 | -- | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 58.0 | -- | °C | ISO 75-2/A |
| CLTE - Flow | 1.1E-4 | -- | cm/cm/°C | ASTM D696 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VITAMIDE® AY36BK8513 | Jackdaw Polymers | Nylon 66 | VITAMIDE® |
| Titalon® 2150 | Titan Plastics Compounds Co., Ltd. | Nylon 66 | Titalon® |
| Geon™ Vinyl Rigid Extrusion L6256 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Extrusion |
| Haysite SMC 46000 | Haysite Reinforced Plastics | Polyester, TS | Haysite SMC |
| LEXAN™ EXL1414H resin | SABIC Innovative Plastics | PC | LEXAN™ |