Ultramid® A3L HP BK20465
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bUI1kg_Ultramid-A3L-HP-BK20465.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ultramid A3L HP BK20465 is an unreinforced, heat stabilized, impact modified, high flow, nylon 66 for injection molding. This grade has excellent flow and improved ambient and low temperature toughness. Applications Typical applications include fasteners and clamps. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.10 | -- | g/cm³ | ISO 1183 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 2440 | 1370 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | |||
| Yield, 23°C | 63.0 | 44.0 | MPa | |
| Break, 23°C | 49.0 | 41.0 | MPa | |
| Tensile Strain (Yield, 23°C) | 6.2 | 25 | % | ISO 527-2 |
| Nominal Tensile Strain at Break (23°C) | 28 | > 50 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 2280 | 1150 | MPa | ISO 178 |
| Flexural Stress (23°C) | 85.0 | 45.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | |||
| -30°C | 14 | 11 | kJ/m² | |
| 23°C | 19 | 28 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | |||
| -30°C | No Break | No Break | ||
| 23°C | No Break | No Break | ||
| Notched Izod Impact Strength | ISO 180 | |||
| -40°C | 12 | 9.4 | kJ/m² | |
| 23°C | 18 | 29 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 70.0 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 260 | -- | °C | ISO 3146 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 | °C | |
| Drying Time | 1.0 to 2.0 | hr | |
| Suggested Max Moisture | 0.040 to 0.20 | % | |
| Processing (Melt) Temp | 288 to 305 | °C | |
| Mold Temperature | 60.0 to 100 | °C | |
| Injection Pressure | 35.0 to 125 | MPa | |
| Injection Rate | Fast | ||
| Back Pressure | 0.00 to 0.350 | MPa | |
| Screw Speed | 40 to 80 | rpm | |
| Screw Compression Ratio | 3.0:1.0 to 4.0:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsan® BMNO MED | Arkema | Nylon 11 | Rilsan® |
| RTP 300 TC-C-20 | RTP Company | PC | RTP |
| Teldene® H03BPMP | National Petrochemical Industries Company (NATPET) | PP Homopolymer | Teldene® |
| ELITE™ 5401GS | The Dow Chemical Company | EPE | ELITE™ |
| LEXAN™ ML7647K resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |