Fibrolon® P 8540
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | FKuR Kunststoff GmbH |
| Trademark: | Fibrolon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bUErOf_Fibrolon-P-8540.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Fibrolon® P 8540 (prev. Fibrolon® 46 N) Natural fibre reinforced compound for injection moulding |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ISO 1183 |
| Apparent Density | 0.36 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (190°C/5.0 kg) | 2.0 - 3.0 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (190°C/5.0 kg) | 3.00 - 4.00 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3400 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 26.0 | MPa | ISO 527-2 |
| Fracture | 24.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 4.5 | % | ISO 527-2 |
| Flexural Modulus | 3500 | MPa | ISO 178 |
| Flexural Stress (3.5% Strain) | 41.0 | MPa | ISO 178 |
| Tensile Strain at Tensile Strength | 3.0 | % | ISO 527 |
| Flexural Strain at Break | 6.0 | % | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.6 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 11 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 155 | °C | ISO 306/A |
| Melting Temperature (DSC) | 160 - 180 | °C | ISO 3146 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.30 | % | |
| Rear Temperature | 160 | °C | |
| Middle Temperature | 170 | °C | |
| Front Temperature | 180 | °C | |
| Nozzle Temperature | 180 | °C | |
| Processing (Melt) Temp | 170 | °C | |
| Mold Temperature | 30.0 | °C | |
| Injection Pressure | < 200 | MPa | |
| Injection Rate | Moderate | ||
| Back Pressure | < 5.00 | MPa |
| Injection instructions |
|---|
| Feeding zone: 150°CCylinder kneeling temp: 140°CScrew peripheral velocity: up to 150 mm/sHolding pressure level: 40 to 70%Holding pressure time: 15 to 30 sMelt cushion (of volume): 3 to 10%Cooling time: 10 to 30 s |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 2943-90 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Next Nylon 66 Prime Series PXIM-01NC | Next Polymers Ltd. | Nylon 66 | Next Nylon 66 Prime Series |
| Nypol® PA A3 G40 M3 NTLA014 NR448 MSP | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Hostalen PP H2222 36 | LyondellBasell Industries | PP Impact Copolymer | Hostalen PP |
| LNP™ COLORCOMP™ FR23C compound | SABIC Innovative Plastics | ABS | LNP™ COLORCOMP™ |