Infino AR-5300H
| Category: | PBT+ASA , Polybutylene Terephthalate + ASA |
| Manufacturer: | SAMSUNG SDI CO., LTD. |
| Trademark: | Infino |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bTVtC1_Infino-AR-5300H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Infino AR-5300H is a Polybutylene Terephthalate + ASA (PBT+ASA) product filled with glass fiber. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Typical application: Automotive. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.45 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/5.0 kg) | 30 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow : 3.20 mm | 0.60 | % | ASTM D955 |
| Across Flow : 3.20 mm | 0.60 | % | ISO 2577 |
| Flow : 3.20 mm | 0.30 | % | ISO 2577 |
| Ash Content | |||
| -- | 30 | % | ISO 3451 |
| -- | 30 | % | ASTM D5630 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 117 | ASTM D785, ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 8300 | MPa | ASTM D638 |
| -- | 7000 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 2 | 130 | MPa | ASTM D638 |
| Yield | 110 | MPa | ISO 527-2/50 |
| Break 3 | 130 | MPa | ASTM D638 |
| Break | 105 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Break 4 | 5.0 | % | ASTM D638 |
| Break | 5.0 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 5 | 8800 | MPa | ASTM D790 |
| -- 6 | 7800 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 190 | MPa | ASTM D790 |
| -- 8 | 170 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 8.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 79 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 88 | J/m | ASTM D256 |
| 23°C 10 | 8.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 6.40 mm | 205 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 4.00 mm | 195 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 6.40 mm | 193 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 4.00 mm | 180 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 205 | °C | ISO 306/B50 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 120 | °C | |
| Desiccant Dryer | 120 | °C | |
| Drying Time | |||
| -- | 4.0 | hr | |
| Desiccant Dryer | 4.0 | hr | |
| Suggested Max Moisture | 0.040 | % | |
| Rear Temperature | 230 to 240 | °C | |
| Middle Temperature | 240 to 250 | °C | |
| Front Temperature | 250 to 260 | °C | |
| Nozzle Temperature | 270 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C | |
| Injection Pressure | 98.1 | MPa | |
| Back Pressure | 2.94 to 7.85 | MPa | |
| Screw Speed | 5 to 25 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.8 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | Thickness: 4 mm |
| 10 . | Thickness: 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULADUR® A GF 10 | A. Schulman Europe | PBT | SCHULADUR® |
| Akulon® F249-HG4 | DSM Engineering Plastics | Nylon 6 | Akulon® |
| Colorite Rigid PVC 2018 | Colorite Polymers | PVC, Rigid | Colorite Rigid PVC |
| LONGLITE® PBT 1100-600S | CCP Group | PBT | LONGLITE® PBT |
| MAJORIS G474 | AD majoris | PP, Unspecified | MAJORIS |