Kepital® FC2020H

Category:	Acetal (POM) Copolymer , Acetal (POM) Copolymer
Manufacturer:	Korea Engineering Plastics Co., Ltd
Trademark:	Kepital®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	bSqaEl_Kepital-FC2020H.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Kepital® FC2020H is an Acetal (POM) Copolymer material filled with 20% carbon fiber. It is available in Asia Pacific, Europe, or North America.

Important attributes of Kepital® FC2020H are:

Flame Rated

Chemical Resistant

Creep Resistant

Fatigue Resistant

Good Processability

Typical applications include:

Electrical/Electronic Applications

Engineering/Industrial Parts

Automotive

General Information
Filler / Reinforcement	Carbon Fiber, 20% Filler by Weight
Features	Fatigue Resistant Good Chemical Resistance Good Creep Resistance Good Flow Good Moldability Good Stiffness Good Thermal Stability Good Wear Resistance Good Weather Resistance
Uses	Automotive Applications Electrical Parts Electronic Data Processing Industrial Parts Machine/Mechanical Parts
Forms	Pellets

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.46	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	6.0	g/10 min	ASTM D1238
Molding Shrinkage - Flow	0.40	%	ASTM D955
Water Absorption (24 hr)	0.28	%	ASTM D570

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (M-Scale)	98		ASTM D785

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength	167	MPa	ASTM D638
Tensile Elongation (Break)	3.0	%	ASTM D638
Flexural Modulus	13200	MPa	ASTM D790
Flexural Strength	245	MPa	ASTM D790
Shear Strength	80.3	MPa	ASTM D732

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (3.20 mm)	80	J/m	ASTM D256
Tensile Impact Strength (1.60 mm)	158	kJ/m²	ASTM D1822

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load			ASTM D648
0.45 MPa, Unannealed	164	°C
1.8 MPa, Unannealed	163	°C
Melting Temperature	165	°C
CLTE - Flow	1.5E-6	cm/cm/°C	ASTM D696
RTI Elec (0.800 mm)	50.0	°C	UL 746
RTI Imp (0.800 mm)	50.0	°C	UL 746
RTI Str (0.800 mm)	50.0	°C	UL 746

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	5.0E+5	ohms	ASTM D257
Volume Resistivity	2.0E+5	ohms·cm	ASTM D257

Flammability	Nominal Value	Unit	Test Method
Flame Rating (0.800 mm)	HB		UL 94

Resin Grade	Manufacturer	Category	Trademark
Maxxam™ PPH-40C Nat	PolyOne Corporation	PP Homopolymer	Maxxam™
RTP 2700 S-40A	RTP Company	SEBS	RTP
Moplen HP740T	PolyMirae	PP Random Copolymer	Moplen
Karina BLACK PVC COMPOUND 804-48/ 1-CRE	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina
XENOY™ X4820 resin	SABIC Innovative Plastics	PC+PBT	XENOY™