Geon™ BIO RA551S
| Category: | PVC, Flexible , Flexible Polyvinyl Chloride |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Geon™ BIO |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bRtbDB_Geon-BIO-RA551S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A Cellular flexible vinyl formulated to achieve a minimum level of 25% bio-based content and classified as a PolyOne Sustainable Solution |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- 1 | 0.758 | g/cm³ | |
| -- 2 | 1.10 | g/cm³ |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness 3(Shore A, 15 sec) | 50 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Break | 7.58 | MPa | |
| 100% Strain | 3.10 | MPa | |
| Tensile Elongation (Break) | 410 | % | ASTM D638 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature 4 | -45.0 | °C | ASTM D746 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 166 to 171 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 160 to 166 | °C |
| Note Message | |
|---|---|
| 1 . | Blown test specimen(24 hrs. @ 90C.) |
| 2 . | Solid test specimen |
| 3 . | Solid test specimen. |
| 4 . | Solid test specimen |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAROLOX 10 K4 | Taro Plast S.p.A. | PBT | TAROLOX |
| Chemlon® 125 G | Teknor Apex Company (Chem Polymer) | Nylon 66 | Chemlon® |
| ExxonMobil™ HDPE HD 7845.30 | ExxonMobil Chemical | HDPE, UHMW | ExxonMobil™ HDPE |
| LONGLITE® PBT 3015-200S | CCP Group | PBT | LONGLITE® PBT |
| PLUSTEK PA303G5 | Polyram Ram-On Industries | Nylon 66 | PLUSTEK |