NORYL™ SE1GFN1 resin

Category: PPE+PS , Polyphenylene Ether + PS
Manufacturer: SABIC Innovative Plastics
Trademark: NORYL™
Fillers: -
Ports: Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms FOB, CIF, DAP, DAT, DDP
PDF: bRdHux_NORYLSE1GFN1resin.pdf
PRICE: ​Order Products​ email   sales@su-jiao.com
Wechat: WECHAT
Message
NORYL SE1GFN1 is a 10% glass reinforced, injection moldable modified polyphenylene ether resin. Designed for improved dimensional stability and good flow , this resin also uses non-chlorinated, non-brominated FR additives to achieve a V1 UL94 rating at 1.0 mm and UL94 5VA rating @ 2.5 mm. NORYL SE1GFN1 has a GWIT of 775C@ 1.00 mm according to IEC 60695-2-13, and a CTI > 250 V according to IEC 60112 (Color dependant). NORYL SE1GFN1 may be an excellent material candidate for electrical or electronic applications requiring good rheological properties, heat resistance, hydrolysis resistance, low density and thin wall flame resistance. SE1GFN1 is halogen free according to VDE/DIN 472 part 815.
General Information
Filler / Reinforcement
  • Glass fiber reinforced material, 10% filler by weight
Additive
  • Flame retardancy
Features
  • Chlorine Free
  • Good dimensional stability
  • Low density
  • Good liquidity
  • Heat resistance, medium
  • Hydrolysis resistance
  • Bromine-free
  • Flame retardancy
Uses
  • Electrical/Electronic Applications
Agency Ratings
  • DIN VDE 0472 part 815
RoHS Compliance
  • RoHS compliance
Processing Method
  • Injection molding
PhysicalNominal ValueUnitTest Method
Specific Gravity
    -- 1.16g/cm³ASTM D792
    -- 1.17g/cm³ISO 1183
Melt Volume-Flow Rate (MVR) (280°C/10.0 kg)15.0cm³/10minISO 1133
Molding Shrinkage - Flow 10.30 - 0.50%Internal method
Water Absorption ISO 62
    Saturated, 23°C 0.22%ISO 62
    Equilibrium, 23°C, 50% RH 0.070%ISO 62
HardnessNominal ValueUnitTest Method
Ball Indentation Hardness (H 358/30)100MPaISO 2039-1
MechanicalNominal ValueUnitTest Method
Tensile Modulus 4000MPaISO 527-2/1
Tensile Stress ISO 527-2/5
    Yield 75.0MPaISO 527-2/5
    Fracture 70.0MPaISO 527-2/5
Tensile Strain ISO 527-2/5
    Yield 2.5%ISO 527-2/5
    Fracture 3.0%ISO 527-2/5
Flexural Modulus 23000MPaISO 178
Flexural Stress 110MPaISO 178
Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel)50.0mgInternal method
ImpactNominal ValueUnitTest Method
Charpy Notched Impact Strength 3ISO 179/1eA
    -40°C 5.1kJ/m²ISO 179/1eA
    -30°C 5.2kJ/m²ISO 179/1eA
    23°C 6.1kJ/m²ISO 179/1eA
Charpy Unnotched Impact Strength ISO 179/1eU
    -30°C 430kJ/m²ISO 179/1eU
    23°C 530kJ/m²ISO 179/1eU
Notched Izod Impact ISO 180/1A
    -40°C 66.2kJ/m²ISO 180/1A
    -30°C 76.2kJ/m²ISO 180/1A
    23°C 87.1kJ/m²ISO 180/1A
Unnotched Izod Impact Strength 9ISO 180/1U
    -30°C 25kJ/m²ISO 180/1U
    23°C 25kJ/m²ISO 180/1U
ThermalNominal ValueUnitTest Method
Heat Deflection Temperature 10
    0.45 MPa, unannealed, 100 mm span 140°CISO 75-2/Be
    1.8 MPa, unannealed, 100 mm span 135°CISO 75-2/Ae
Vicat Softening Temperature
    -- 145°CISO 306/A50, ISO 306/B120
    -- 140°CISO 306/B50
Ball Pressure Test IEC 60695-10-2
    125°C PassIEC 60695-10-2
    135°C 11PassIEC 60695-10-2
Linear thermal expansion coefficient
    Flow : -40 to 40°C 5.5E-4cm/cm/°CASTM E831, ISO 11359-2
    Flow : 23 to 80°C 5.0E-5cm/cm/°CISO 11359-2
    Lateral : -40 to 40°C 6.8E-5cm/cm/°CASTM E831, ISO 11359-2
    Lateral : 23 to 80°C 7.0E-5cm/cm/°CISO 11359-2
Thermal Conductivity 0.27W/m/KISO 8302
RTI Elec 110°CUL 746
RTI Imp 105°CUL 746
RTI 110°CUL 746
ElectricalNominal ValueUnitTest Method
Surface Resistivity > 1.0E+15ohmsIEC 60093
Volume Resistivity 1.0E+15ohms·cmIEC 60093
Dielectric Strength IEC 60243-1
    0.800mm, in oil 33kV/mmIEC 60243-1
    1.60mm, in oil 26kV/mmIEC 60243-1
    3.20mm, in oil 16kV/mmIEC 60243-1
Relative Permittivity IEC 60250
    50 Hz 2.80IEC 60250
    60 Hz 2.80IEC 60250
    1 MHz 2.70IEC 60250
Dissipation Factor IEC 60250
    50 Hz 5.0E-3IEC 60250
    60 Hz 5.0E-3IEC 60250
    1 MHz 3.0E-3IEC 60250
Comparative Tracking Index 250VIEC 60112
Needle Flame Test 12(1.50 mm)PassIEC 60695-11-5
High Voltage Arc Tracking Rate (HVTR) PLC 4UL 746
FlammabilityNominal ValueUnitTest Method
Flame Rating UL 94
    1.00 mm, Testing by SABIC V-1UL 94
    1.50 mm V-1UL 94
    2.50 mm, Testing by SABIC 5VAUL 94
Glow Wire Flammability Index (1.00 mm)960°CIEC 60695-2-12
Glow Wire Ignition Temperature IEC 60695-2-13
    1.00 mm 775°CIEC 60695-2-13
    2.00 mm 800°CIEC 60695-2-13
    3.00 mm 800°CIEC 60695-2-13
Oxygen Index 30%ISO 4589-2
InjectionNominal ValueUnit
Drying Temperature 100 - 120°C
Drying Time 2.0 - 3.0hr
Hopper Temperature 60.0 - 80.0°C
Rear Temperature 240 - 260°C
Middle Temperature 260 - 280°C
Front Temperature 280 - 300°C
Nozzle Temperature 260 - 280°C
Processing (Melt) Temp 280 - 300°C
Mold Temperature 80.0 - 120°C
Note Message
1 .Tensile Bar
2 .2.0 mm/min
3 .80*10*3 sp=62mm
4 .80*10*3 sp=62mm
5 .80*10*4 sp=62mm
6 .80*10*3
7 .80*10*4
8 .80*10*4
9 .80*10*4
10 .120*10*4 mm
11 .Approximate maximum
12 .10 sec
Resin Grade Manufacturer Category Trademark
RTP 3400 MG-350 RTP Company LCP RTP
SABIC® LLDPE 6335BE Saudi Basic Industries Corporation (SABIC) LLDPE SABIC® LLDPE
Shandong PP/PE PP/PE Alloy Shandong Dongchen Engineering Plastics Co., Ltd. PP+PE Shandong PP/PE
LNP™ THERMOTUF™ VF006U compound SABIC Innovative Plastics Nylon, Unspecified LNP™ THERMOTUF™
apilon 52® ETC 40 API SpA TPU-Polyether apilon 52®