ASTALOY™ PC/PET C70L9S
| Category: | PC+PET , Polycarbonate + PET |
| Manufacturer: | Marplex Australia Pty. Ltd. |
| Trademark: | ASTALOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bRNiPA_ASTALOY-PC-PET-C70L9S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ASTALOY™ PC/PET C70L9S is an alloy of Polycarbonate (PC) and Polyethylene Terephthalate (PET) polymer which features extremely high impact strength, a high chemical resistance, high rigidity, high processing thermal stability and heat resistance. Note: The letter "U" indicates UV stabilisation has been added [ ie: ASTALOY™ PC/PET C70L9US]. |
| General Information | |
|---|---|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 20 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 0.70 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.10 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 112 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.20 mm) | 59.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | > 180 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 2250 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 86.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 900 | J/m | ASTM D256 |
| Dart Drop Impact (3.20 mm) | 100 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 1.8 MPa, unannealed, 3.20mm | 112 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 118 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 12.7mm | 124 | °C | ASTM D648 |
| Vicat Softening Temperature | 155 | °C | ASTM D1525 5 |
| CLTE - Flow | 6.5E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Flammability Index (1.60 mm) | 750 | °C | AS/NZS 60695 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 140 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Rear Temperature | 250 - 260 | °C | |
| Middle Temperature | 260 - 270 | °C | |
| Front Temperature | 270 - 280 | °C | |
| Processing (Melt) Temp | 270 - 290 | °C | |
| Mold Temperature | 60.0 - 90.0 | °C | |
| Injection Pressure | 60.0 - 140 | MPa | |
| Injection Rate | Slow-Moderate | ||
| Back Pressure | 0.300 - 1.00 | MPa | |
| Clamp Tonnage | 4.0 - 8.0 | kN/cm² |
| Injection instructions |
|---|
| Screw Speed: Minimum |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 压 力1 (10N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pyramid™ II230 | Polymics, Ltd. | PEI | Pyramid™ |
| Sylvin 2910-80 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| EXCEVAL™ AQ-4104 | Kuraray Co., Ltd. | EVA | EXCEVAL™ |
| ExxonMobil™ LLDPE LL 6100.17 | ExxonMobil Chemical | LLDPE | ExxonMobil™ LLDPE |
| Petrotene® PP A3 T40 HS UV PRTA010 PH382 MSP | Petropol Industry and Trade of Polymers LTDA | PP Homopolymer | Petrotene® PP |