Nistil F35
| Category: | SAN , Styrene Acrylonitrile |
| Manufacturer: | Soredi S.p.a. |
| Trademark: | Nistil |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bR9WeF_Nistil-F35.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Copolymer styrol-acrylonitrile with 35% glass fibre, suitable for the injection moulding of items requiring high stiffness. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.35 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.20 to 0.30 | % | ASTM D955 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.050 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 124 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break) | 110 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 2.0 | % | ASTM D638 |
| Flexural Modulus 3 | 11500 | MPa | ASTM D790 |
| Flexural Strength 4(Break) | 155 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 50 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 105 | °C | ASTM D648 |
| Vicat Softening Temperature | 110 | °C | ASTM D1525 5 |
| CLTE - Flow (23 to 55°C) | 2.5E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Relative Permittivity (1 MHz) | 2.40 | IEC 60250 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | HB | ||
| 3.20 mm | HB |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Wondel® A AG6I | Nanjing Julong Engineering Plastics Co., LTD | Nylon 66 | Wondel® A |
| ENFLEX S3185AE | ENPLAST Americas, a Ravago Group Company | TPE | ENFLEX |
| GLAMIDE® T-663G15 | TOYOBO America, Inc. | Nylon 66 | GLAMIDE® |
| Osterlene® PPC-57-1.4-N | Osterman & Company | PP Impact Copolymer | Osterlene® |
| Sylvin 5175-92 White 1489 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |